Electrodeposition of aluminum from AlCl3-NaCl-KCl molten salt

JingSheng Li,Zhanhong Yang,Xiaohua Wang,Wangxing Li,Jianhua Chen,Shengwei Wang,Jingwei Li
2008-01-01
Abstract:Silvery bright aluminum coating was obtained on iron substrate from 0.66-0.17-0.17 (mole ratio) AlCl3-NaCl-KCl molten salt at various cathode current densities. The microstructure of the coating was investigated by SEM and XRD, and the mechanism of electrodeposition was illuminated by cyclic voltammogram. The results show that when cathode current density is 25 mA/cm2, aluminum coating is acicular and (200) plane structure is reliable to be formed. The maximal current efficiency of 92% is obtained when current density is 40 mA/cm2 and it decreases sharply after current density is over 80 mA/cm2. When cathode current density is 60 mA/cm2, the obtained aluminum crystalline grain is a mixture of acicular and spherical, aluminum coating has (111) cubic structure. When current density is 100 mA/cm2, spherical aluminum coating is reliable to be formed. The thickness of aluminum coating increases with prolongation of plating time and the increase of cathode current density. The deposition is obtained owing to the reduction of which has a peak value of -0.23 V.
What problem does this paper attempt to address?