Research on Preparation and Electric Properties of KxNa1-xNbO3 Lead-Free Piezoelectric Ceramics

Qin Bo,Tan Guoqiang,Xia Ao

2011-01-01

Rare Metal Materials and Engineering

Abstract:Potassium sodium niobate (KxNa1-xNbO3) powders were prepared by solid phase synthesis, and the KxNa1-xNbO3 ceramics were fabricated by pressureless sintering. The effect of the composition, sintering temperature and polarizing voltage on the phase composition of the powders and density, electrical properties of the ceramics were investigated. The results show that when x = 0.5, sintering temperature was 1050 degrees C and the polarization voltage was 3 kV/mm, KxNa1-xNbO3 ceramics with good piezoelectric properties (relative density reaches 94%, piezoelectric constant d(33) = 105 pC/N, planar electromechanical coupling coefficient k(p) = 0.39, dielectric loss tan delta = 0.29, mechanical quality factor Q(m) = 45, and dielectric constant epsilon(r) = 720) can be prepared. With the increasing polarization voltage, ceramic piezoelectric properties are increased, and the polarization basically reaches saturation when the polarization voltage E = 3 kV/mm.