Abstract:Anomalous eutectics are argued to form due to the remelting of the primary solid during solidification of deeply undercooled eutectic alloy melts. As an indicator of the tendency for anomalous eutectic formation, the remelted fraction of the primary eutectic was analyzed systematically based on the eutectic dendrite growth theory. For eutectic alloys with either larger equilibrium solute distribution coefficients or gentle liquidus slopes, the primary eutectic is highly supersaturated with solute and more prone to remelting. When the eutectic composition is set to different values, (e.g. the eutectic point is closer to one phase of the eutectic), the two eutectic phases under rapid growth change their compositions simultaneously, but their remelted fractions during temperature recalescence do not vary significantly. Three representative binary eutectic alloys Ag–39.9at.%Cu, Ni–19.6at.%P and Pd–16.0at.%P – their eutectic products are solid solution–solid solution, solid solution–stoichiometric intermetallic compound and stoichiometric intermetallic compound–stoichiometric intermetallic compound, respectively, were solidified at large undercooling. Anomalous eutectics were observed in the first two eutectic alloys whose eutectic structure consists of at least one solid solution phase, whereby the stoichiometric intermetallic compound phase remained highly oriented whereas the solid solution phase had a near random distribution of orientations. For the Pd–16.0at.%P alloy, however, the primary eutectic retained its original morphology as the final solidification structure regardless of the degree of undercooling. All these experimental results validate the argument that anomalous eutectics result from the remelting of the primary solid.

Formation Mechanism of Anomalous Eutectics in Highly Undercooled Ag-39.9 At%Cu Alloys

Investigation of the Origin of Anomalous Eutectic Formation by Remelting Thin-Gauge Samples of an Ag-Cu Eutectic Alloy

The Formation Mechanism of Anomalous Eutectic in Highly Undercooled Ni-Sn Eutectic Alloy

Solidification behavior and microstructure of Ag–Cu eutectic alloy at different sub-rapid cooling rates

Cellular Growth of Lamellar Eutectics in Undercooled Ag–Cu Alloy

Non-equilibrium solidification of bulk undercooled Ni–P eutectic alloys

Remelting-induced Anomalous Eutectic Formation During Solidification of Deeply Undercooled Eutectic Alloy Melts

Anomalous Eutectic Formation in the Solidification of Undercooled Co–Sn Alloys

Mechanism of Anomalous Eutectic Formation in the Solidification of Undercooled Ni–Sn Eutectic Alloy

Microstructure Refinement Mechanism of Undercooled Cu55Ni45 Alloys

Solidification of Undercooled Ag–Cu Eutectic Alloy with the Sb Addition

Anomalous eutectics in intermediately and highly undercooled Ni-29.8at.%Si eutectic alloy

Anomalous Eutectic Formation in Undercooled Ni−P Eutectic Alloy

Mode of Dendrite Growth in Undercooled Alloy Melts

Evolution Mechanism of Rapid Solidification Microstructure of an Undercooled Copper-Based Single Phase Alloy

Growth Velocity-Undercooling Relationship and Structure Refinement Mechanism of Undercooled Ni-Cu Alloys

The Formation of Quasiregular Microstructure in Highly Undercooled Ni(70.2)Si(29.8) Eutectic Alloy

Solidification Microstructure Evolution and Grain Refinement Mechanism under High Undercooling of Undercooled Ni90Cu10 Alloys

Rapid Solidification Structure Refinement Mechanism in Highly Undercooled Cu Based Ternary Alloys

Solidification Microstructure in a Supercooled Binary Alloy

Formation of Single-Phase Supersaturated Solid Solution Upon Solidification of Highly Undercooled Fe–Cu Immiscible System