Abstract:Multiple ion-doped lithium manganese oxides LiCr x Ni x Mn 2-2x O 4-z F z (0 < x ≤ 0.25, z = 0.05, 0.1) with a spinel structure and space group Fd 3 m were prepared by using the co-precipitation procedure carried out in water–alcohol solvent using adipic acid as the chelating agent. The electrochemical measurements indicated that the charge/discharge capacities of the samples prepared at 600 °C are higher than that of the treatment at 800 °C or microwave heating. The capacitance-voltage (CV) curves of LiCr x Ni x Mn 2-2x O 4-z F z (0 < x ≤ 0.25, z = 0.05, 0.1) showed that when x ≤ 0.1, the samples had two reduction–oxidation peaks at 4.0 to 4.2-V region, whereas when x > 0.1, the samples had only one reduction–oxidation peak at 4.0- to 4.2-V region in CV measurements and could offer more stable voltage plateau in a 4-V region and also had stable electrical conductivity after 20 cycles. Another reduction–oxidation peak appeared in 4.6-4.8-V region (Ni 2+ –Ni 4+ reduction–oxidation peaks); this suggests that the LiCr x Ni x Mn 2-2x O 4-z F z (0.1 < x ≤ 0.25, z = 0.05, 0.1) cathode material could offer 4.6 to 4.8-V charge/discharge plateaus, and its specific capacity increases with increasing Ni 2+ . The impedance measurements of the cell proved that the F − anion doped can not only prevent Mn 3+ from disproportion but also can prevent the passivation film from forming and can help keep stable the cell’s electrical properties. The LiCr 0.05 Ni 0.05 Mn 1.9 O 3.9 F 0.1 sintered at 600 °C shows the best cycle performance and the largest capacity in all prepared samples; its first discharge capacity is 120 mAh/g, and the discharge capacity loses only 1.78

Preparation Conditions of LiMn_(0.45)Ni_(0.45)Co_(0.1)O_2 Via Hydroxide Co-precipitation

Preparation and Electrochemical Properties of Li[Ni1/3Co1/3Mn1−x/3Zrx/3]O2 Cathode Materials for Li-ion Batteries

Effect of fluorine in the preparation of Li(Ni1/3Co1/3Mn1/3)O2 via hydroxide co-precipitation

Enhanced electrochemical performance of F-doped Li<sub>1.2</sub>Mn<sub>4/6</sub>Ni<sub>1/6</sub>Co<sub>1/6</sub>O<sub>2.35</sub> cathode materials for Li-ion batteries

Synthesis and electrochemical performance of LiNi_(1/3)Mn_(1/3)Co_(1/3)O_2-zFz cathode materials for lithium ion batteries

Synthesis of High Tap-Density Layered LiMn0.4 Ni0.4 Co0.2 O2 Cathode Material

Enhanced Electrochemical Performance of F-doped Li1.2Mn4/6Ni1/6Co1/6O2.35 Cathode Materials for Li-ion Batteries

High capacity 0.5Li2MnO3·0.5LiNi 0.33Co0.33Mn0.33O2 cathode material via a fast co-precipitation method

LiNbO3 Coating and F- Doping Stabilize the Crystal Structure and Ameliorate the Interface of LiNi0.88Co0.06Mn0.03Al0.03O2 to Improve the Electrochemical Properties and Safety Capability

Effect of Mn Doping on the Structure and Electrochemical Performance of LiNi0.7Co0.3O2

Effect of Cationic (Na+) and Anionic (F−) Co-Doping on the Structural and Electrochemical Properties of LiNi1/3Mn1/3Co1/3O2 Cathode Material for Lithium-Ion Batteries

Al, B, and F doped LiNi1/3Co1/3Mn1/3O2 as cathode material of lithium-ion batteries

Effects of Al doping on the electrochemical performances of LiNi0.83Co0.12Mn0.05O2 prepared by coprecipitation

Improvement of LiNi<sub>1/3</sub>Co<sub>1/3</sub>Mn<sub>1/3</sub>O<sub>2</sub> Cathode Materials by Nano-MgO Doping

Co-precipitation synthesis and performance of multi-doped LiCr x Ni x Mn 2-2x O 4-z F z cathode materials for lithium ion batteries

Advanced Electrochemical Performance of Li[Ni(1/3−x)FexCo1/3Mn1/3]O2 As Cathode Materials for Lithium-Ion Battery

Investigation of Li 3 PO 4 Coating and Nb 5+ Doping Effect on the Crystal Structure and Electrochemical Properties of Ni-Rich LiNi 0.85 Co 0.05 Mn 0.10 O 2 Cathode

Effects of Abundant Co Doping on the Structure and Electrochemical Characteristics of LiMn1.5Ni0.5−xCoxO4

Synthesis and Characterization of M-doped Li1.05Co0.3Ni0.35Mn0.3O2 (M=Zn, Fe, Ti, Zr) Cathode Materials for Lithium ion Battery

Synthesis and Electrochemical Properties of Li[Ni X Co Y Mn 1− X − Y ]O 2 ( X, Y = 2/8, 3/8) Cathode Materials for Lithium Ion Batteries

Synthesis And Characterization Of Li(Li0.2mn0.4fe0.2m0.2)O-2 (M=Co, Ni, Cr, Al) Cathode Materials For Li-Ion Batteries