Effects of thermal treatment on precipitate shape and mechanical properties of Mg-8Gd-4Y-Nd-Zr alloy

Xinming Zhang,Changping Tang,Yunlai Deng,Liu Yang

DOI: https://doi.org/10.1016/j.matdes.2011.06.033

IF: 9.417

2011-01-01

Materials & Design

Abstract:Precipitation reactions in a Mg-8Gd-4Y-Nd-Zr alloy have been investigated using TEM, HREM, hardness measurements and tensile testing. Globular β′ precipitates, which were different from the typical plate-shaped β′ precipitates usually observed in Mg-Gd-based alloys, were detected in the 160°C/192 h-aged sample. Instead of dissolution and then precipitating as plate-shaped β′ precipitates, the formed globular β′ precipitates grew up when further aged at 215°C, which resulted in the decrease in strength comparing with that of the 215°C single-stage aged samples. Two-stage ageing treatments on the alloy demonstrated that ageing 192 h at 150°C plus 16 h at 215°C made the ultimate strength and the yield strength improved 17 MPa and 13 MPa, respectively.