DEVELOPMENT OF HYDROGENATED SBR-BASED VULCANIZATES WITH SUPERIOR TIRE TREAD PERFORMANCE
Tuhin Dolui,Jagannath Chanda,Prasenjit Ghosh,Rabindra Mukhopadhyay,Shib Shankar Banerjee
DOI: https://doi.org/10.5254/rct.24.00014
IF: 2.081
2024-07-24
Rubber Chemistry and Technology
Abstract:ABSTRACT Currently, the tire industry is exploring eco-friendly tires with improved rolling resistance, traction, abrasion resistance, and fatigue properties. By investigating the potential of hydrogenated SBRs (HSBRs) as a tire tread material, a special and modified grade of SBR was developed. The rheological, mechanical, and dynamic mechanical properties and abrasion, fatigue, aging, and ozone resistances of the developed HSBR-based composites were critically evaluated and compared with those of conventional rubber–based compounds, such as NR, emulsion SBR (ESBR), and solution SBR (SSBR). Interestingly, the HSBR-based vulcanizates exhibited superior modulus, tensile strength, abrasion resistance, fatigue crack growth resistance, resistance to thermo-oxidative aging, and ozone resistance compared with conventional SBR–based vulcanizates. The modulus at 300% elongation of the HSBR-based vulcanizates was approximately 74 and 11% higher than that of the ESBR- and SSBR-based composites, respectively, whereas the improvements in tensile strength were approximately 88 and 64% and the improvements in abrasion resistance were approximately 250 and 200% that of ESBR and SSBR, respectively. The tensile strength and fatigue resistance characteristics of the HSBR vulcanizates were also nearly similar to those of the NR vulcanizate. The findings demonstrate that HSBR can be a potential tire tread material with robust physico-mechanical properties and durability.
polymer science