Abstract:Niobium fluoride (NbF5) is introduced into the MgH2 + 1/4AlH(3) hydride composite by ball milling to improve the hydrogen desorption properties of the Mg-Al-H system. It is found that after being ball milled with 1 mol % of NbF5, AlH3 in the composite has almost fully decomposed and forms metallic Al, which indicates that NbF5 can significantly destabilize AlH3. DSC results show that NbF5 addition also helps reduce the peak desorption temperature of MgH2 in the composite from 324 to 280 degrees C. Isothermal desorption measurements demonstrate that MgH2 in the doped composite can rapidly release 98% of its hydrogen after desorption at 300 degrees C for 1 h, while the valued is only 46% for the undoped composite. The activation energy for hydrogen desorption of MgH2 in the doped composite is calculated to be 104.5 kJ/mol, much lower than that in the undoped composite (127.4 kJ/mol). These results suggest that NbF5 addition dramatically improves the hydrogen desorption kinetics of the MgH2 + 1/4AlH(3) composite. Dehydrogenation hydrogenation measurements reveal that the hydrogen desorption kinetics of the undoped composite declines with cycle number, whereas the NbF5-doped composite maintains good cycling stability. Microstructure studies indicate that the decline of the kinetics is attributed to the grain growth and particle agglomeration of MgH2 during hydrogen sorption cycling. However, NbF5 addition can suppress this grain growth through the formation of Nb/NbH layers surrounding the particles of MgH2 and acting both as the impediment to grain growth of Mg/MgH2 and as the gateway for hydrogen diffusion. Finally, the role that AlH3 plays in the hydrogen desorption process of the Mg-Al-H composites is discussed.

Structural and hydriding properties of composite Mg–ZrFe1.4Cr0.6

Hydriding Properties of a Mechanically Milled Mg–50 Wt.% ZrFe1.4Cr0.6 Composite

Direct hydrogenation of Mg and decomposition behavior of the hydride formed

Hydrogen Storage Properties of Mg+10% TiFe_(1-x)Cr_x(x=0,0.3) Multi-Phase Alloys

Microstructure and Hydrogen Storage Characteristics of Nanocrystalline Mg+xwt% LaMg2Ni (x=0–30) Composites

Enhanced hydrogen sorption properties of MgH2 when doped with mechanically alloyed amorphous Zr0·67Ni0.33 particles

Effect of Mn And Zr on Hydrogen Absorption in Mg-Based Nanocomposites

Microstructures And Hydrogen Desorption Properties Of The Mgh2-Alh3 Composite With Nbf5 Addition

Influence of composite ball-milling with Ti0.9Zr0.1Mn1.5 on hydrogen storage properties of Ti9.6V86.4Fe4 alloy

Hydrogen Storage Behaviors and Microstructure of MF3 (m=ti, Fe)-doped Magnesium Hydride

Enhanced Hydrogen Storage Properties of MgH2 by the Synergetic Catalysis of Zr0.4Ti0.6Co Nanosheets and Carbon Nanotubes

Phase-structure and Hydrogen Storage Behaviors of Mg+10％ Ni2P Composite Prepared by Reactive Ball-Milling

Study on the Dehydrogenation Properties and Reversibility of Mg(Bh4)(2)-Alh3 Composite under Moderate Conditions

Optimizing FeCoNiCrTi High-Entropy Alloy with Hydrogen Pumping Effect to Boost De/hydrogenation Performance of Magnesium Hydride

The Hydriding and Dehydriding Properties of Some Multicomponent Rare-Earth Magnesium Alloys

Preparation and hydrogen storage properties of Mg-20 wt.% Mg 2Ni0.8Cr0.2 composite with TiO2 nanoparticles

Hydrogen Sorption Properties of Mg-20wt. % Fe23y8 Composite Prepared by Reactive Mechanical Alloying

Properties of Hydriding and Dehydriding of Nanocrystalline Composite of Mg-Ni-Cr2O3

Hydrogen desorption behaviour and microstructure evolution of a γ-AlH3/MgCl2 nano-composite during dehydriding

Preparation and Hydrogen Storage Properties of Mg-20 Wt.% Mg<sub>2</sub>Ni<sub>0.8</sub>Cr<sub>0.2</sub> Composite with TiO<sub>2</sub> Nanoparticles

Enhancement in Dehydriding Performance of Magnesium Hydride by Iron Incorporation: A Combined Experimental and Theoretical Investigation