Rehydrogenation and cycling studies of dehydrogenated NaAlH4

Dalin Sun,Sesha S Srinivasan,Guorong Chen,Craig M Jensen

DOI: https://doi.org/10.1016/j.jallcom.2003.10.043

IF: 6.2

2004-01-01

Journal of Alloys and Compounds

Abstract:The hydrogenation reaction of NaH+1/3Al+1/2H2↔1/3Na3AlH6+2/3Al+H2↔NaAlH4 was studied in the temperature range of 80–170°C and the pressure range of 8–12MPa. It was found that under the pressure of 12MPa, an increase in the hydrogenation temperature from 100 to 170°C causes a reduction in the amount of absorbed hydrogen. Under the constant pressure of 10MPa, the initial rate of hydrogenation increases when the temperature increases from 80 to 120°C, and reaches an optimum at 120°C; further increase in temperature leads to a decrease in the rate. It was also observed that at a constant temperature, the rate increases with the increase of applied hydrogen pressure. The cycling studies of titanium doped NaAlH4 have shown that the initial capacity was about 3.6wt.%, but after a few dehydrogenation–rehydrogenation cycles, the capacity decreases to 3.0wt.%. And this capacity was retained with no further deterioration in the following consecutive 100 cycles. However, the rates of the two-step dehydrogenation processes were found to reduce kinetically with the ongoing cycling.