Abstract:The formation mechanism of α″-Fe16N2 phase was investigated in the form of nanoparticles. Both α-Fe and γ-Fe2O3 nanoparticles were used to prepare α″-Fe16N2 by using a low-temperature nitriding process (≤180 °C). The synthesized α″-Fe16N2 nanoparticles have a high α″-Fe16N2 volume ratio up to 93%, with a specific saturation magnetization of 178 emu/g (room temperature) and coercivity of 2.0 kOe. The formation of α″-Fe16N2 phase includes three stages: (1) the heterogenous nucleation of α″-Fe16N2 with simultaneous chemical reaction, (2) the growth of α″-Fe16N2 with a local electric field in the Fe16N2 layer, and (3) the termination of Fe16N2 growth due to the nucleation of other Fe–N phases (ε-Fe3N or γ′-Fe4N). In low-temperature nitriding, NH3 was used as the nitrogen source. The adsorbed NH3 molecules on the Fe surface decompose into N and H atoms, and then N atoms react with Fe and nucleation of α″-Fe16N2 simultaneously occurs at the high-energy surface sites of reduced Fe nanoparticles. The growth of α″-Fe16N2 phase can be explained by the electric field modified diffusion theory, where the electric field is established by the migration of Fe and N ions and electrons. Finally, the nucleation of Fe–N stable phases (ε-Fe3N or γ′-Fe4N) ceases the further growth of α′′-Fe16N2 layer. Then, there is critical thickness for the α″-Fe16N2 layer, which is estimated to be 10–15 nm from the surface. Therefore, single-phase α″-Fe16N2 nanoparticles are expected in fine particles with less than 30 nm in diameter.

Synthesis Process and Growth Mechanism of Γ′-Fe 4 N Nanoparticles by Phase-Transformation

Magnetic Properties and Thermal Stability of Γ′-Fe4n Nanoparticles Prepared by a Combined Method of Reduction and Nitriding

Influence of Different Preparation Methods on Crystallisation and Morphology of Fe2o3 Nanoparticles

Massive transformation in FeNi nanopowders with nanotwin-assisted nitridation

Preparation and Magnetic Properties of Nanoscale Ɛ-Fe3n Particles.

Critical Thickness of Α″-Fe16n2 Layer Prepared in Low-Temperature Nitriding

Preparation of Α′-Fe(n)/α′-fe8n by Γ′-Fe4n Precursor

Preparation Of The Single-Phase Gamma'-(Fe1-Xnix)(4)N Compounds (0-Less-Than-Or-Equal-To-X-Less-Than-Or-Equal-To-0.6)

Magnetic Properties and Thermal Stability of Nanocrystalline Ε-Fe3n Prepared by Gas Reduction-Nitriding Method

Synthesis and Characterization of Fe/C Core–shell Nanoparticles

Chemical Synthesis of Monodisperse Fe-Ni Nanoparticles Via A Diffusion-Based Approach

Surface modification and characterization of γ-Fe2O 3 nanoparticles synthesized by chemically-induced transition

Preparation of CNTs-supported Fe3O4 and Fe3C Nano-particles and the Investigation on their Magnetic Properties

Growth and Properties of Single-Crystalline Γ-Fe2o3 Nanowires

Strain-induced Phase-Structure of Fe2O3 Nanoparticles

Preparation of Composite Nanoparticles of Fe-Zn Bioxide Using Surface Modification and Their Subsequent Characterization

Controllable Synthesis of Hollow Α-Fe2o3 Nanostructures, Their Growth Mechanism, and the Morphology-Reserved Conversion to Magnetic Fe3O4/C Nanocomposites

The Chemistry of Spinel Ferrite Nanoparticle Nucleation, Crystallization, and Growth

In-situ Observation on the Isothermal Decomposition Process of Γ-Fe[n] by X-ray Diffraction

Synthesis and characterization of Fe–Ti nanoparticles by nitrogen plasma metal reaction

The Structure of Modified Fe-Ni Bioxide Composite Nanoparticles Using Fe(NO 3 ) 3