Abstract:Oxy-apatite lanthanum silicates with general formula La 10 Si 5.9 M 0.1 O 27±δ (M = Cr 3+ , Mn 4+ , Fe 3+ , Mo 6+ , W 6+ ; 0.05 ≤ δ ≤ 0.1, coded LaSiMO) were obtained by gel-combustion and they were characterized through electrochemical impedance spectroscopy. The XRD patterns show that all samples adopt apatite structure and crystallize in the hexagonal space group P-3(147) with crystallite sizes ranging from 86 nm to 103 nm. The dopant cations were accommodated at Si position with the highest occupancy factor at O6 sites (responsible in conduction) for LaSiCrO and LaSiFeO apatites. Fe and Cr doped samples contain pure apatite phase while those doped with Mn, Mo, W contain La 2 SiO 5 as secondary phase which act as insulator in conduction process. Based on EPR and ICP-OES investigations we found that Mn, Mo, W cations present multiple oxidation states in the apatite lattice and a lower incorporation degree in comparison with Fe and Cr cations. Local distortions are present in Fe and Cr doped apatite lattices which explains the higher ionic conductivity of these samples. At 500 o C, the ionic conductivities, range between 1.15·10 − 4 and 3.56·10 − 4 S·cm − 1 for samples sintered at 1400 o C, values that are higher than un-doped apatite (6.46·10 − 5 S·cm − 1 ). Due to the highest ionic conductivity among the samples, LaSiCrO was additionally sintered at 1500 o C and 1600 o C in order to investigate the role of temperature on ionic conduction process. The relative density of LaSiCrO was improved from 89.03 to 93.06% and the ionic conductivity reach 0.28·10 − 2 S·cm − 1 , at 600 o C. The results of this study show that apatites doped with Cr and Fe may be used as electrolytes in SOFCs.

Synthesis and electrical properties of apatite-type La10Si6O27

The effect of local structure on ionic conductivity of apatite-type La9.5Si6O26.25

Studies on morpho-structure and ionic conductivity of apatite-type lanthanum silicate doped with transitional metal cations

Sol-gel synthesis and ionic conductivity of oxyapatite-type La 9.33+xSi6O26+1.5x

SPS preparation of La10Si6O27 and the effect of sintering temperature on electrical conductivity

Synthesis and sintering of LaPO4 powder and its application

Enhanced electrical conductivity of P-doped apatite-type lanthanum silicate solid electrolytes and analysis of the mechanism

Sintered La10−xNdxSi6O27 (x = 0, 0.1, 0.2, 0.3) by spark plasma sintering and its microstructure and electrical conductivity

Enhanced oxide-ion conductivity in highly c-axis textured La10Si6O27 ceramic

Highly Enhanced Electrical Conductivity in Electrospun La9.6Si6O26.4 Nanofibres

Synthesis and Thermal Performance of RE9.33(SiO4)(6)O-2 Ceramics

Preparation and Properties of Perovskite La1-xSrxCoO3-delta Powders and Ag-LSCO Electrical Contact Composite Materials

Preparation of Mesoporous La2Sn2O7 Powder and Ag-La2Sn2O7 Electrical Contact Composite Materials and Their Properties

Crystal chemistry and ionic conductivity of garnet-type solid-state electrolyte, Li 5- x La 3 (NbTa)O 12- y

Electrical Conductivity of Sr and Ti doped LaCrO3 Ceramics

Low temperature sintering and enhanced piezoelectricity of lead-free (Na 0.52 K 0.4425 Li 0.0375)(Nb 0.86 Ta 0.06 Sb 0.08) O 3 ceramics prepared from nano-powders

Electrical Properties of Ce0.8Sm0.1Nd0.1O2-delta/La10Si6O27 Composite Electrolytes

Influence of La3+, Ce4+ on phase transition and sintering property of cordierite material prepared by solid reaction

Hydrothermal Synthesis and Dielectric Properties of Lanthanum Titanate Ceramics

An extremely low thermal conduction ceramic: RE 9.33(SiO 4) 6O 2 silicate oxyapatite

Preparation of nanosized la2CuO4 particle by chemical precipitation method and its thermoelectrical properties