Cerium(Ⅲ) Film Formation Process for Aluminum Alloys Observed with Electrochemical Impedance Spectroscopy

Gu Baoshan,Liu Jianhua
DOI: https://doi.org/10.3321/j.issn:1000-4343.2007.02.015
2007-01-01
Abstract:Electrochemical impedance spectroscopy(EIS) of B95 aluminum alloy in 0.01 mol·L-1 CeCl3 solution was investigated to study the film formation and mechanism.Typical EIS spectrum changes were clearly observed during the film formation processes.EIS results indicated that Ce(Ⅲ) film can form on the aluminum surface by chemical treatment.EIS was used for in situ and continuously to observe the formation of cerium when aluminium alloy was immersed in 0.01 mol·L-1 CeCl3 solution.Research was done on the process of film formation and mechanism of B95 aluminum alloy through the changes of EIS in the process.Followed was analysis on the tested EIS based on equivalent circuit.The result showed that the variation of EIS can clearly display the film change of B95 aluminum alloy in cerium solution.The film formation process of RE conversion film can be divided into three stages: formation stage,growth stage and stable equilibrium stage.The formation stage mainly involved the solution of aluminum alloy.In growth stage,the conversion film was gradually thickening with the lapse of time and the solution of aluminum alloy was inhibited.In stable equilibrium stage,the film growth and solution had reached a balance.The analysis of EIS showed that the conversion film developed in natural environment was not compact and EIS equivalent circuit in this stage was identical to that in growth stage,but the impedance spectrum contained two time constants.Based on the three stages the film formation model was proposed,meanwhile,the EIS equivalent circuit and the impedance expressions in different stages were also presented.
What problem does this paper attempt to address?