Cyclic Performance Of Waste-Derived Sio2 Stabilized, Cao-Based Sorbents For Fast Co2 Capture
Feng Yan,Jianguo Jiang,Kaimin Li,Sicong Tian,Zongwen Liu,Jeffrey Shi,Xuejing Chen,Jingyuan Fei,Yuxiang Lu
DOI: https://doi.org/10.1021/acssuschemeng.6b01903
IF: 8.4
2016-01-01
ACS Sustainable Chemistry & Engineering
Abstract:Calcium-looping technology has been identified as one of the most favorable CO2 capture techniques for the implementation of carbon capture, utilization, and storage (CCUS); however, the rapid deactivation of CaO sorbents due to sintering is currently a major barrier of this technology. We report for the first time an environmentally benign and cost-effective strategy to reduce sintering by adding waste-derived nanosilica, synthesized from photovoltaic waste (SiCl4), into Cao-based sorbents through a simple dry mixing procedure. The as-synthesized sorbent (90% CaCO3-W) resulted in final CO2 uptake of 0.32 g(CO2) g(CaO)(-1) within 5 min of carbonation. Even under the most severe calcination conditions (at 920 degrees C in pure CO2), it still maintained a stable capture capacity, with CO2 uptake of 0.23 g(CO2) g(CaO)(-1) after 30 cycles. Additionally, the CO2 uptake percentage reached similar to 90% in the fast carbonation stage (similar to 20 s), which is of great significance for real applications. The most likely stabilization mechanism was considered on the basis of N-2 physisorption isotherms and X-ray diffraction patterns. It was concluded that stable and refractory larnite (Ca2SiO4) particles were formed during 2-h thermal pretreatment at 900 degrees C, leading to sintering resistance. This strategy significantly enhanced the cyclic stability and carbonation rate of CaO-based sorbents through the reuse of SiCl4 and is thus a green technology for scaled-up fast CO2 capture.