Solid-Liquid Two-Phase Flow Erosion Wear Properties of Si3N4-SiC Composite

Ding Hewei,Liu Baolin,Gao Deli,Huang Zhaohui,Fang Minghao,Wu Xiaoxian,Chen Bo,Liu Yangai

DOI: https://doi.org/10.3321/j.issn:1002-185X.2009.z2.056

2009-01-01

Rare Metal Materials and Engineering

Abstract:Si3N4-SiC composites were fabricated from the compact of Si powder and SiC formed by cold isostatic pressing via reactive sintering in nitrogen atmosphere. And contrast experiments of liquid-solid two-phase erosion-wear were taken with 95Al(2)O(3) wear resistant ceramic using water and SiC particles as erosion medium. The results showed that erosion-wear resistance of samples with the addition of 40 similar to 80wt% Si powder was better than that of 95Al(2)O(3) wear resistant ceramic. And the sample with the addition of 70wt% Si powder possessed an optimum liquid-solid two-phase erosion-wear property. The erosion rate were only 0.87% and 0.30% under a line speed of 132 m/min and 67 m/min, respectively.