The impact of Ni and Mo on growth-morphology and mechanical properties of arc evaporated Ti-Cr-N hard coatings
A.V. Chernogor,F.F. Klimashin,A.O. Volkhonskii,I.V. Blinkov,P.H. Mayrhofer
DOI: https://doi.org/10.1016/j.surfcoat.2019.124917
IF: 4.865
2019-11-01
Surface and Coatings Technology
Abstract:<p>We studied the growth-morphology, structure, mechanical and tribological properties of Ti<sub>0.43</sub>Cr<sub>0.57</sub>N<sub>0.92</sub>, Ti<sub>0.35</sub>Cr<sub>0.65</sub>N<sub>0.78</sub>/Ni<sub>0.003</sub>, and Ti<sub>0.13</sub>Cr<sub>0.74</sub>Mo<sub>0.13</sub>N<sub>0.71</sub>/Ni<sub>0.025</sub> coatings synthesized by cathodic arc evaporation. The Ni-free and low-Ni-containing coatings, Ti<sub>0.43</sub>Cr<sub>0.57</sub>N<sub>0.92</sub> and Ti<sub>0.35</sub>Cr<sub>0.65</sub>N<sub>0.78</sub>/Ni<sub>0.003</sub>, are characterized by a dense columnar growth-morphology and coherent growth of Ti-rich and Cr-rich layers (due to the two-fold substrate rotation). The addition of only 0.3 at% Ni to the growing film results in a significant grain refinement, increased compressive stresses (from −6.7 to −9.7 GPa), and increased hardness (from 25 to 43 GPa). These two coatings show a high cohesive strength with crack formation during scratch tests for loads above 75 N. The Ni-richer and Mo-containing coating, Ti<sub>0.13</sub>Cr<sub>0.74</sub>Mo<sub>0.13</sub>N<sub>0.71</sub>/Ni<sub>0.025</sub>, also exhibits a dense growth-morphology with a layered structure. The higher Ni content of 2.5 at% leads to metallic Ni formation, allowing the growth of films with low compressive stresses of only −0.6 GPa and still a comparably high hardness of 30 GPa. The Ni segregated to grain and column boundaries weakens their cohesive strength (allowing to relax the growth induced stresses), and crack formation can already be observed for loads of 25 N during the scratch tests. However, their performance during pin-on-disk tests at 550 °C is superior – with a lower coefficient of friction of 0.45 and lower wear rate of 0.4 · 10<sup>−</sup><sup>6</sup> mm<sup>3</sup>/(N·m) – to the other two coatings.</p>
physics, applied,materials science, coatings & films