Bamboo-Based Activated Carbon for DCFC Prepared by KOH Activation

ZHONG Zhao-Ping,ZHANG Ju-Bing,GUO Hou-Kun,FU Zong-Ming,XIAO Jian-Min
2011-01-01
Journal of Engineering Thermophysics
Abstract:Activated carbon for DCFC from bamboo with KOH activation was prepared in this paper.The influence of activation temperature,activation time and the ratio of KOH to carbon on BET surface area were investigated.The activated carbon was catalyzed by nickel to improve the electrical conductivity and then treated with HNO_3 solution to realize the surface modification and ash removal.Its performance was evaluated in a DCFC anode.The optimum conditions for activated carbon preparation were listed as follows:activation temperature,800℃:activation time,1h;ratio of KOH to carbon,3;nickel loading,2%;loading temperature,900℃;holding time,2 h;and HNO_3 solution concentration,4 mol·LT~(-1).The activated carbon with BET surface area of 2295 m~2·g~(-1), electrical resistivity of 6963μΩ·and ash content of 3.58%was prepared under such conditions.The performance of DCFC anode with bamboo-based activated carbon as fuel was better than that using other carbon fuels(activated carbon fiber and graphite).
What problem does this paper attempt to address?