Abstract:series of aluminophosphate-based tubular mesoporous molecular sieves without (UHM-1) and with substituted silicon (UHM-3) have been synthesized at room temperature in the presence of a cationic surfactant cetyltrimethylammonium chloride (CTACl) and an organic base tetramethylammonium hydroxide (TMAOH). Characterization by powder X-ray diffraction (XRD), electron probe microanalysis (EPMA), transmission electron microscopy (TEM), N-2 adsorption, and Al-27, P-31, and Si-29 magic-angle-spinning (MAS) NMR spectroscopies has been carried out to understand both the pore structures and the local atomic arrangements of these solid products. The synthesis of UHM-1 and UHM-3 is successful only at room temperature within the following molar gel composition: Al2O3:(0.6-3.4) P2O5:(0.0-1.0) SiO2:(0.24-0.50) CTACl:(8.5-47.0) TMAOH:(200-642) H2O. The presence of TMAOH is essential to maintain the gel pH at 8.5 or above. The pH greatly influences the nature of the final "crystalline" products, particularly the coordination of aluminum and phosphorus. XRD, EPMA, TEM, and N-2 adsorption measurements show that these solid products have a unique composition and disordered tubular mesopores with an average pore diameter of about 35 Angstrom in the calcined form. The overall P/Al ratio of UHM-1 is less than unity, especially in gels of higher pH, indicating incomplete condensation of phosphorus and a nonideal aluminophosphate framework. This may account for their poorer thermal stability relative to microporous aluminophosphate molecular sieves and aluminosilicate-based MCM-41 materials. Al-27 and P-31 MAS NMR reveal that aluminum in UHM-1 with a P/Al ratio of 0.60 synthesized at a gel pH of 8.5 is present in both tetrahedral and octahedral environments while phosphorus is present in a tetrahedral environment and also as hydroxylated species. As the P/Al ratio of UHM-1 decreases together with increasing gel pH, the relative amounts of tetrahedral aluminum and tetrahedral phosphorus decrease. This change suggests some Al-O-P linkages in the tetrahedral regions of the UHM-1 samples, and an increasing octahedral aluminum content st lower P/Al ratio indicates that octahedral aluminum alone can construct a tubular mesoporous structure. After incorporation of silicon into UHM-1, Si-29, Al-27, and P-31 MAS NMR of UHM-3 reveal that silicon is atomically dispersed and that the relative amounts of tetrahedral aluminum and tetrahedral phosphorus increase monotonically with increasing silicon incorporation. Virtually all the aluminum is tetrahedral, and all the phosphorus is tetrahedral after silicon incorporation reaches a Si/Al ratio of unity. This indicates more ordered atomic arrangements of tetrahedral silicon, aluminum, and phosphorus via oxygen bridges in UHM-3 than in UHM-1. The incorporation of silicon appears to make the aluminophosphate framework more flexible and facilitates the formation of an aluminophosphate-based mesoporous structure.

Thermally Stable Mesoporous Aluminophosphates Assembled from Preformed Precursors of Microporous Aluminophosphate

A Stable Hexagonal Mesoporous Aluminophosphate Assembled from Preformed Aluminophosphate Precursors

Block Copolymer Templating Syntheses of Ordered Large-Pore Stable Mesoporous Aluminophosphates and Fe-aluminophosphate Based on an “acid–base Pair” Route

Synthesis of Thermally Stable Mesoporous Hexagonal Aluminophosphate Molecular Sieves

Mesoporous Aluminophosphates and Fe-Aluminophosphates with Highly Thermal Stability and Large Surface Area Templated from Semi-Fluorinated Surfactant

Multinuclear solid-state NMR studies on the formation mechanism of aluminophosphate molecular sieves in ionic liquids

One-step synthesis of large pore mesoporous metallo-aluminophosphates under nonaqueous media

Obtaining of Mesoporous Aluminosilicates with High Hydrothermal Stability by Composite Organic Templates: Utility and Mechanism

Vapor Phase Transport Synthesis and Structure Characterization of an Aluminophosphate Molecular Sieve [Al3P3O12F][C5H5NH]center dot 0.2H(2)O

"Solvent-free" synthesis of thermally stable and hierarchically porous aluminophosphates (SF-APOs) and heteroatom-substituted aluminophosphates (SF-MAPOs)

Strongly Acidic and High-Temperature Hydrothermally Stable Mesoporous Aluminosilicates with Ordered Hexagonal Structure

Tetramethylguanidine-templated Synthesis of Aluminophosphate-Based Microporous Crystals with AFI-type Structure

Characterization of Aluminophosphate-Based Tubular Mesoporous Molecular Sieves

Synthesis and characterization of ordered mesoporous aluminosilicates molecular sieves with highly hydrothermal stability

Synthesis of the Molecular-Sieve Alpo4-5 with an Unequal Molar Ratio of Al2o3 to P2o5

One-step synthesis of hydrothermally stable mesoporous aluminosilicates with strong acidity

Preparation of a Hierarchically Porous AlPO4monolith Via an Epoxide-Mediated Sol–gel Process Accompanied by Phase Separation

Synthesis, Characterization, and Catalytic Properties of Stable Mesoporous Aluminosilicates Assembled from Preformed Zeolite L Precursors

Facile Synthesis for Ordered Mesoporous Gamma-Aluminas with High Thermal Stability

New Understanding and Simple Approach to Synthesize Highly Hydrothermally Stable and Ordered Mesoporous Materials

Preparation of mesoporous Al-MCM-41 with stable tetrahedral aluminum using ionic liquids as a single template