Abstract:The pristine and Mg-substituted LaAlO3 perovskites were synthesized by the citrate sol-gel method and employed as supports for Ni catalysts in CO2 reforming of methane. The Mg/La molar ratio of 2/8 was determined as the optimal amount of Mg substitution in Ni/La1-xMgxAlO3-δ catalysts. Compared with the Ni/LaAlO3 catalyst, the Ni/La0.8Mg0.2AlO2.9 catalyst exhibited enhanced initial activity and improved stability. Structural characterizations including N2 sorption (N2 sorption), X-ray diffraction (XRD), transmission electron microscopy (TEM), energy-dispersive X-ray spectrometry (EDX) elemental mapping, thermogravimetry-differential scanning calorimetry (TG-DSC), CO2 temperature-programmed desorption (CO2-TPD), X-ray photoelectron spectroscopy (XPS) and H2 temperature-programmed reduction (H2-TPR) were performed to elucidate the effect of Mg partial substitution. It is revealed that much smaller Ni nanoparticles were formed with Mg partial substitution, which may explain the enhanced reforming activity. The improved stability over the Ni/La0.8Mg0.2AlO2.9 catalyst was rationalized with better anti-coke and anti-sintering properties, which was closely related with surface basicity, oxygen vacancies and metal-support interactions. The present work demonstrates that perovskites with appropriate surface modification can serve as novel supports for the preparation of highly active catalysts.

Syngas production from methane reforming with O<sub>2</sub> and CO<sub>2</sub> over Ni–La<sub>2</sub>O<sub>3</sub>/SiO<sub>2</sub> catalysts using EDTA salt precursors

Syngas production from methane reforming with O 2 and CO 2 over Ni–La 2 O 3 /SiO 2 catalysts using EDTA salt precursors

Combined Carbon Dioxide Reforming and Partial Oxidation of Methane to Syngas over Ni−La<sub>2</sub>O<sub>3</sub>/SiO<sub>2</sub>Catalysts in a Fluidized-Bed Reactor

Combined Carbon Dioxide Reforming and Partial Oxidation of Methane to Syngas over Ni−La2O3/SiO2 Catalysts in a Fluidized-Bed Reactor

Highly Active and Stable Lanthanum‐doped Core–Shell‐structured Ni@SiO2 Catalysts for the Partial Oxidation of Methane to Syngas

Syngas Production from Reforming of Methane with Co2 and O-2 over Ni/Sro-Sio2 Catalysts in A Fluidized Bed Reactor

Preparation of Novel Mesoporous LaFeO3-SBA-15-CTA Support for Syngas Formation of Dry Reforming

Combination of CO2 reforming and partial oxidation of methane to produce syngas over Ni/SiO2 and Ni–Al2O3/SiO2 catalysts with different precursors

Methane reforming to syngas over LaNi x Fe 1−x O 3 (0≤ x ≤1) mixed-oxide perovskites in the presence of CO 2 and O 2

Syngas Production Via Combined Oxy-Co2 Reforming of Methane over Gd2O3-modified Ni/SiO2 Catalysts in a Fluidized-Bed Reactor

A highly active Ni catalyst supported on Mg-substituted LaAlO3 for carbon dioxide reforming of methane

Catalytic conversion of CH4 and CO2 to synthesis gas on Ni/SiO2 catalysts containing Gd2O3 promoter

Catalytic conversion of methane and CO2 to synthesis gas over a La2O3-modified SiO2 supported Ni catalyst in fluidized-bed reactor

Combination of CO2 reforming and partial oxidation of methane to produce syngas over Ni/SiO2 prepared with nickel citrate precursor

Specific Features Concerning the Mechanism of Methane Reforming by Carbon Dioxide over Ni/La2O3Catalyst

Syngas Production from CO2 Reforming with Methane over Core-Shell Ni@SiO2 Catalysts

Production of Synthesis Gas Via Methane Reforming with Co2 on Ni/Sio2 Catalysts Promoted by Alkali and Alkaline Earth Metals

Syngas Production from Methane Steam Reforming and Dry Reforming Reactions over Sintering-Resistant Ni@SiO2 Catalyst

Partial Oxidation Of Methane To Syngas Over Ni-Based Catalysts

Studies on nickel-based catalysts for carbon dioxide reforming of methane

Thermodynamic and mechanism study of syngas production via integration of nitrous oxide decomposition and methane partial oxidation in the presence of 10%NiO–La0.3Sr0.7Co0.7Fe0.3O3−δ