Abstract:It is imperative to enhance the mechanical properties and corrosion resistance of magnesium (Mg)-based metallic glasses for orthopedic implants to further their development. The addition of yttrium (Y) significantly improves both of these characteristics. The Mg 52.5 Zn 40.5 Ca 5 Y 2 alloy was chosen for its optimal glass-forming capabilities, as evidenced by thermodynamic parameter, P HHS . This alloy demonstrates remarkable enhancements in both mechanical and corrosion properties, despite the presence of a stable Mg 12 YZn phase in the liquid, which precludes the complete formation of glass. The Mg 52.5 Zn 40.5 Ca 5 Y 2 alloy exhibits a substantial increase in hardness, surpassing the Mg 66 Zn 30 Ca 4 metallic glass by up to 30 HV. The compressive strength of this alloy is 690 MPa, which is approximately 138 MPa greater than that of the Mg 66 Zn 30 Ca 4 alloy. The Mg 52.5 Zn 40.5 Ca 5 Y 2 alloy exhibits a higher noble corrosion potential and a lower corrosion current density demonstrating a corrosion current density of 6.970 μA/cm 2 and a corrosion potential of − 1.240 V. These values suggest a significant increase in corrosion resistance when contrasted with the baseline alloy, Mg 66 Zn 30 Ca 4 . The primary cause of this improvement in mechanical behavior and corrosion resistance is the formation of Mg 12 YZn long-period stacking ordered (LPSO) phases and Mg 3 YZn 6 icosahedral phases. The material's overall strength and durability are enhanced by these phases, rendering it a promising candidate for applications that necessitate high performance in both mechanical and corrosive environments. As per the results, Mg 52.5 Zn 40.5 Ca 5 Y 2 alloy is an exceptional choice for advanced material applications due to its distinctive phase composition, which results in superior properties.

Determination of Critical Thickness for Glass Formation in New Easy Glass Forming Magnesium-Base Alloys by the Wedge Chill Casting Technique

Easy Glass Formation in Magnesium-Based Mg-Ni-Nd Alloys

Evaluation of Glass Formation and Critical Casting Diameter in Al-Based Metallic Glasses

Chill-cast in Situ Composites in the Pseudo-Ternary Mg–(Cu,Ni)–Y Glass-Forming System: Microstructure and Compressive Properties

Biodegradable Mg–Zn–Ca–Y Glass-Forming Alloy with an Amendment in Mechanical Properties and Corrosion Resistance

High Glass-Forming Ability Correlated with Fragility of Mg–Cu(Ag)–Gd Alloys

Easy Glass-Formation In Mg64ni21nd15 By Bridgman Solidification

A New Mg 65 Cu 7.5 Ni 7.5 Zn 5 Ag 5 Y 10 Bulk Metallic Glass with Strong Glass-Forming Ability

Ductile behavior and excellent corrosion resistance of Mg-Zn-Yb-Ag metallic glasses

Mg–Ni–(Gd,Nd) Bulk Metallic Glasses with Improved Glass-Forming Ability and Mechanical Properties

A new Mg65Cu7.5Ni7.5Zn5Ag 5Y10 bulk metallic glass with strong glass-forming ability

A Bulk Amorphous Mg62cu28y12 Alloy By Injection-Casting

Thermal Stability, Glass-Forming Ability and Mechanical Properties of Mg-Y-Zn-Cu Glassy Alloys

Production and Mechanical Properties of Roll Bonded Bulk Metallic Glass/Aluminum Laminates

Design and Characterization of Biodegradable Mg-Zn-Ag Metallic Glasses

Formation, Microstructure, and Mechanical Properties of in Situ Mg-Ni-(Gd,Nd) Bulk Metallic Glass Composite

Formation, Structure and Properties of Bulk Metallic Glasses

Mg-based Bulk Metallic Glass Composites with Plasticity and High Strength

Doubling the Critical Size for Bulk Metallic Glass Formation in the Mg−Cu−Y Ternary System

Study on glass-forming ability and corrosion performance of Ca-based biomedical materials

Glass Formability, Thermal Stability and Mechanical Properties of La-Based Bulk Metallic Glasses