Abstract:The paper comprehensively describes the evolution of metastable microstructures in a cast low-Ta-containing γ-TiAl alloy during cooling-tempering-lamellarization heat treatments. The behavior and mechanism of microstructure refinement are discussed. The rapid cooling generates metastable microstructures, including Widmanstätten, feathery, and massive structures, with many γ variants in small sizes and different orientations. It significantly refines the coarsened colonies and randomizes the texture. The tempering can effectively stabilize the metastable microstructures. During tempering, the γ→α phase transformation is more active at higher temperatures while coarsening and recrystallization dominate at lower temperatures. After tempering, a refined microstructure with spherical grains and convoluted structures forms. Subsequent lamellarization treatment optimizes the microstructure and obtains a fine-grained nearly-lamellar microstructure with small colonies (∼70 μm) and dispersed fine γ grains (∼10 vol%), which yielded a 1.0 % elongation with a 487 MPa yield strength (0.2%) and a 589 MPa ultimate tensile strength at room temperature. Finally, the unique promotion effects and mechanism of a small amount of Ta addition on the nucleation, growth, evolution, and stabilization of metastable microstructures are concluded and discussed, which is crucial for the refinement of cast γ-TiAl alloy by heat treatment alone.

Control of a fine-grained microstructure for cast high-Cr TiAl alloys

Microstructure refinement of cast TiAl alloys by β solidification

Control of the homogeneity of the lamellar structure of a TiAl alloy refined by heat treatment

Grain refinement of a TiAl alloy by heat treatment through near gamma transformation

Tensile properties and fracture toughness of TiAl alloys with controlled microstructures

A new α + β Ti-alloy with refined microstructures and enhanced mechanical properties in the as-cast state

Compositional and Microstructural Optimization and Mechanical-Property Enhancement of Cast Ti Alloys Based on Ti-6Al-4V Alloy

Versatility of trace nano-TiC–TiB2 in collaborative control of solidification-rolling-welding microstructural evolution in Al–Mg–Si alloy for enhanced properties

Metastable microstructure evolution and grain refinement in a Low-Ta containing γ-TiAl alloy through heat treatment

Grain refinement of 1 at.% Ta-containing cast TiAl-based alloy by cyclic air-cooling heat treatment

Microstructure refinement of a TiAl alloy by beat treatment

Microstructure Transformation of a Refined High Nb Containing TiAl Alloy

On the grain size refinement of TiAl alloys by cyclic heat treatment

Alloying Design of Titanium Aluminum Intermetallics and Research Progress

Achieving fine fully lamellar microstructure of casting TiAl alloy by simple heat treatment

Microstructure and Properties of a Beta-Solidifying TiAl-based Alloy with Different Refiners

A Newly Generated Nearly Lamellar Microstructure in Cast Ti-48Al-2Nb-2Cr Alloy for High-Temperature Strengthening

Novel Casting TiAl Alloy with Fine Microstructure and Excellent Performance Assisted by Ultrasonic Melt Treatment

Increased tensile strength and elongation of the Ni–Fe based polycrystalline cast superalloy via the trace addition of TiC nanoparticles

A Novel Method and Mechanism for Simultaneously Refining Microstructure and Controlling Grain Orientation in Ti48Al2Cr2Nb2.5C Alloy

Refining grain size of a TiAl alloy by cyclic heat treatment through discontinuous coarsening