Abstract:Cu-WS 2 composites are being used as self-lubricating materials for various engineering applications. The poor wettability between Cu and WS 2 is a main obstacle for obtaining high-performance Cu-WS 2 . In order to improve the wettability, a thin Cu layer was deposited on the surface of the WS 2 powder through an electroless plating technology. Cu-WS 2 composites were prepared via spark plasma sintering (SPS) using the mix powders of Cu and Cu-WS 2 . Microstructure, mechanical properties and tribological properties of the Cu-WS 2 composites were investigated, and that of the Cu were also comparatively studied. Results show that the WS 2 powder coated with Cu (abbreviated as WS 2 @Cu powder) improves the poor wettability between Cu and WS 2 and meanwhile the distribution of WS 2 . Cu-WS 2 composites sintered below 750 °C could reduce the reaction between Cu and WS 2 and ensure more WS 2 in the composites. Both the coefficient of friction (COF) and the wear rate of the Cu-WS 2 are lower than that of the Cu. A lubricant film leads to the excellent tribological properties as the Cu-WS 2 composites were tested at 25−200 °C. However, the disappearance of WS 2 and the formation of Cu 2 O cause to the decreasing self-lubricating performances at 300−500 °C. With an increase in the test temperature, the dominant wear mechanisms of the Cu-WS 2 composites change from adhesive wear to a mixture of abrasive and oxidation wear, and that of the Cu change from adhesive wear to a mixture of fatigue and oxidation wear.

Preparation and Tribological Properties of WS_2-C Solid Lubrication Films

Tribological Properties of WS2 Composite Film Prepared by a Two-Step Method

Microstructure and Tribological Properties of Co-sputtered MoS2/WS2 Composite Films

Microstructure and Tribological Behavior of WS2–Ag Composite Films Deposited by RF Magnetron Sputtering

Microstructure, Chemical and Tribological Investigations of Mo X W1−x S Y Co-Sputtered Composite Films

Tribological performance of a tungsten disulfide lubricant film prepared by atomic layer deposition using tungsten hexacarbonyl and hydrogen sulfide as precursors

Microstructure and Tribological Behavior of the WS_2-Ag Composite Films Deposited by Radio Frequency Magnetron Sputtering in Different Environments

Microstructure, chemical and tribological investigations of Mo<sub><i>x</i></sub>W<sub>1−<i>x</i></sub>S<sub><i>y</i></sub> co-sputtered composite films

Effect of Ag Content on Microstructure and Tribological Performance of WS2–Ag Composite Films

Friction and Wear Properties of Sputtered WS2/Ag Nanocomposite Films in Different Environments

Microstructures and tribological properties on the composite MoS2 films prepared by a novel two-step method

Interactive effect between WS2 films with different structures and space oils for improvement of tribological performance

Microstructure and Tribological Properties of Ws2/Mos2 Multilayer Films

Dry sliding tribological properties of Cu-WS 2 self-lubricating composites at 25–500 °C

Preparation and Tribological Properties of WS2 Solid Lubricating Coating with Dense Structure Using HiPIMS

Tribological behavior and microstructural evolution of lubricating film of silver matrix self-lubricating nanocomposite

Preparation and tribological properties of Mo/MoS2-Pb-PbS composite films

Microstructure and Tribological Properties of Sputtered MoSx-W Composite Films Supported by Porous Alumina Aperture Array

Study on the Tribological Properties of FeS Solid Lubrication Films Prepared by Two-Step Method

WC-Ni-Cr-based Self-Lubricating Composites Fabricated by Pulsed Electric Current Sintering with Addition of WS2 Solid Lubricant

Tribological Behavior of SiC Coating on C/C Composites Against SiC and WC under Unlubricated Sliding