Abstract:In the current study, a 3-D microscopic structural finite element (FE) model of interpenetrating SiC/Al composites (SiC/Al IPCs) is built, based on X-ray tomography and optimized methods for 3-D mesh generation. In addition, an interface model is introduced into the 3-D FE model to investigate the effects of the interfaces on the damage and failure processes, which includes a “tie-break contact” method at the SiC/Al interfaces. Subsequently, FE methods are applied to investigate the dynamic compression response of the 3-D FE model. To validate the numerical simulation results, the dynamic compression responses of SiC/Al IPCs are measured at strain rates of 2000s−1 using a split Hopkinson pressure bar device. Our results show that failure of the SiC phase occurs just before the effective stress reaches its peak, but it plays a leading role in bearing the pre-metaphase stage of the load. From the point of energy dissipation, however, the contribution of Al phase cannot be ignored in the final stage of failure because the residual Al phase absorbs 30% of the energy of the global model by plastic deformation, even though its mass failure ratio is only 2%. Further microanalysis shows that the cracks initiate and propagate mainly near the SiC/Al interface, just on the side of the SiC ceramic phase. As the cracks extend further into the SiC phase, there appears a new “interface debonding” failure mode. These results show that brittle fracture of the SiC ceramic phase plays a key role in crack initiation, since the presence of complex 3-D SiC/Al interfaces usually causes the generated cracks to deflect before interconnecting with each other. This significantly retards propagation of the cracks, and thus increases the ductility of the composite materials. In the final stage of failure, the cracks are interconnected with each other in the SiC phase while the Al phase still maintains a degree of structural integrity. It is found that there exists obvious plastic deformation in local, relatively narrow, regions in the Al phase, and the local necking and tearing fractures tend to be localized in these severely deformed regions. Numerical simulation results are consistent with the observed behavior.

Dynamic Observation of Fracture Process in A Silicon Carbide-Matrix Laminated Ceramic Composite

In-situ Observation of Crack Evolution in Ti/Al Laminated Composite

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

Damage Evolution and Fracture Behavior of C/SiC Minicomposites with Different Interphases under Uniaxial Tensile Load

Micro/nanoscale mechanical characterization and in situ observation of cracking of laminated Si3N4/BN composites

In-situ study of the fracture behavior of SiCf/SiC composite material under three-point bending

Real-Time Observation of Damage Nucleation in Three-Dimensionally Reinforced Carbon/Carbon Composites and Role of Bundle/Matrix Interface

In Situ Damage Propagation and Fracture in Notched Cross-Ply SiC/SiC Composites: Experiment and Numerical Modeling

Dynamic Fracture Process and Strain Rate Effect of a Porous SiC Ceramic

Study of mechanical properties and cracking extension resistance behavior of C/SiC composites by single edge notched beam and digital image correlation techniques

Fractural Process and Toughening Mechanism of Laminated Ceramic Composites

In-plane Mechanical Behavior and Failure Mode of a 2D-Sic/sic Composite under Uniaxial Dynamic Compression

Study on Behavior of Dynamic Fracture in SiC Nanoparticles Reinforced Magnesium Matrix Composites

2D-Sicf/sic Interlaminar Mode I Fracture Testing and Characterization

Damage and failure analysis of a SiCf/SiC ceramic matrix composite using digital image correlation and acoustic emission

Matrix Cracking of 2D SiC/SiC Composite Characterized by in Situ SEM and Nano-Ct

Simulation of Damage and Failure Processes of Interpenetrating SiC/Al Composites Subjected to Dynamic Compressive Loading

Dynamic Crack Propagation from a Circular Defect in a Unidirectional Carbon Fiber Reinforced Plastic Composite

Study on Fracture Behavior of BN- SiC Laminated Composite Ceramics

In Situ Crack Growth Observation and Fracture Behavior of Short Carbon Fiber Reinforced Geopolymer Matrix Composites

Fracture behavior of multlayer SiC/C composites