Abstract:Carbon-fiber reinforced composites are made up of three different phases. Tensile or compressive deformation in the longitudinal (fiber) orientation is controlled by the fibers, leading to a linear stress strain response which ends abruptly when the fibers fail by tensile fracture or kinking in compression. Conversely, major non-linear deformations can develop under transverse compression or in-plane shear because deformation is controlled by the polymeric matrix and the interphase.In this paper, first the V-notched rail shear test was used to research the mechanical properties of composite under in-plane shear loading, and the fracture surfaces of failed specimens were examined using scanning electron microscopy (SEM). The broken samples showed a large residual shear displacement. For [0/90](8s) cross-ply laminate V-notched beam test, the failure mode is the interactions of intralaminar and interlaminar failure. The intralaminar interfacial debonding, matrix cracking and interlaminar degradation occurs in succession. Then a representative volume element (RVE) of fiber random distribution was established, with two dominant damage mechanisms-matrix plastic deformation and interfacial debonding included in the simulation by the extended Drucker-Prager model and cohesive zone model respectively. The simulation results clearly reveal the damage process of the composites and the interactions of different damage mechanisms. It can be concluded that the in-plane shear fracture initiates as interfacial debonding and evolves as a result of interactions between interfacial debonding and matrix plastic deformation. The progressive damage process and final failure mode of in-plane shear model which are based on constitute are very consistent with the observed result under SEM of V-notched rail shear test. Also a transverse shear model was established as contrast in order to comprehensively understand the mechanical properties of composite materials under shear loading, and the progressive damage process and final failure mode of composite under transverse shear loading were researched.

Real-Time Observation of Damage Nucleation in Three-Dimensionally Reinforced Carbon/Carbon Composites and Role of Bundle/Matrix Interface

Interfacial Strengthening and Self-Monitoring in Carbon Fiber-Reinforced Composites via Carbon Nanotube-Based Damage Sensors

In situ Observation of Compression Damage in a Three-Dimensional Braided Carbon Fiber Reinforced Carbon and Silicon Carbide (C/C-SiC) Ceramic Composite

Experimental and Numerical Study on Failure Behaviors of Composite Grid Stiffeners under Tensile and Flexural Loading

Micromechanical Modeling of Damage Evolution and Mechanical Behaviors of CF/Al Composites under Transverse and Longitudinal Tensile Loadings.

A Microcracking-Based Model for the Dynamic Failure of Carbon/carbon Composites

Caustic Investigation of Dynamic Interactions Between Propagating Matrix Crack and Modified Fibre Bundles

Failure behavior and damage visualization of thick carbon/aramid hybrid woven composites under flexural loading conditions

Evaluation of Carbon Fiber/epoxy Interfacial Strength in Transverse Fiber Bundle Composite: Experiment and Multiscale Failure Modeling

Microscopic Progressive Damage And Failure Analysis Of Carbon-Fiber Reinforced Composite Under Shear Loading

Multiscale Analysis of Fracture of Carbon Nanotubes Embedded in Composites

Morphology characterization and in-situ three-dimensional strain field monitor of short carbon fiber-reinforced polymer composites under tension

Damage Evolution and Fracture Behavior of C/SiC Minicomposites with Different Interphases under Uniaxial Tensile Load

In Situ Observation and Modeling of Damage Modes in Cross-Ply Ceramic Matrix Composites

Observation of Damage Initiation for Trans-laminar Fracture Using in situ Fast Synchrotron X-ray Radiography and ex situ X-ray Computed Tomography

3D Orthogonal Woven Carbon/Carbon Composites: Micromechanical Modeling and Damage Analysis

In-situ characterization on the fracture behavior of three dimensional polymer nanocomposites reinforced by CNT sponge

Frictional Sliding of Microcracks under Compression

Multiscale Image-Based Modelling of Damage and Fracture in Carbon Fibre Reinforced Polymer Composites

Flexural progressive damage and failure behavior of carbon-aramid/epoxy hybrid woven composites

Characteristics of interfaces in 3D fine weave carbon/carbon composites