Abstract:Crystalline helical carbon nanotubes (HCNTs) are synthesized as the main products in the pyrolysis of acetylene at 450 °C over Fe nanoparticles generated by means of a combined sol–gel/reduction method. Transmission electron microscopy (TEM) images reveal that there are two HCNTs attached to each Fe3C nanoparticle, and that the two HCNTs are mirror images of each other. Annealing in Ar at 750 °C and purification by immersion in hot (90 °C) HCl solution do not significantly change the structure of the HCNTs, despite the partial removal of Fe nanoparticles by the latter treatment. The magnetic properties of the as‐prepared, annealed, and purified HCNTs have been systematically examined. The annealed sample shows relatively high magnetization due to the ferromagnetic α‐Fe nanoparticles encapsulated in the HCNT nodes. In the case of HCl treatment, relatively pure HCNTs are obtained by the removal of ferromagnetic nanoparticles from the double‐HCNT nodes. The effects of the amount of catalyst used in the synthesis process on the morphology and yield of the carbon products have also been investigated.

Synthesis of Helically Coiled Carbon Nanotubes by Reducing Ethyl Ether with Metallic Zinc

A New Method to Fabricate Large Amount of Single-Walled Carbon Nanotubes

Large‐Scale Synthesis of Rings of Bundled Single‐Walled Carbon Nanotubes by Floating Chemical Vapor Deposition

Synthesis of Helical Carbon Nanotubes, Worm-Like Carbon Nanotubes and Nanocoils at 450 °C and Their Magnetic Properties

Synthesis of zinc oxide nanorods using carbon nanotubes as templates

Synthesis Of Large Quantity Single-Walled Carbon Nanotubes By Arc Discharge

Synthesis of carbon nanotubes by reduction of carbon dioxide with metallic lithium

Synthesis of Carbon Nanotubes by Decomposing Alcohol

Large‐Scale Synthesis, Annealing, Purification, and Magnetic Properties of Crystalline Helical Carbon Nanotubes with Symmetrical Structures

Preparation of Large Amounts of Carbon Nanotubes in Hydrogen Atmosphere by Arc-Discharge

A Single‐Step Process to Produce Carbon Nanotube‐Zinc Compound Hybrid Materials

Synthesis,Characterization and Performance of Helical Carbon Nanotubes

Large Scale Synthesis of Single-Wall Carbon Nanotubes by Arc-Discharge Method

Carbon Nanotubes Synthesized By Rapid Quenching Of Red-Hot Graphite Rod In Ethyl Alcohol

A Novel Method to Produce Large Amount Single-Walled Carbon Nanotubes by Arc Discharging

A New Method for Synthesizing Double-Walled Carbon Nanotubes

Large-Scale Synthesis and Magnetic Property of Carbon Nanotubes

A Metal-Reduction Route to Synthesis of Nickel Nanotubules

Large- Scale Production of Single- Walled Carbon Nanotubes Using Fe/Mo/MgO Cryogel Catalyst

Single-source Precursor Route to Carbon Nanotubes at Mild Temperature

Ethylene Flame Synthesis of Well-Aligned Multi-Walled Carbon Nanotubes