Synthesis of Ni_0.6 Cu_0.2 Zn_0.2 Fe_2O_4 via Solid State Reaction at Low Heating Temperatures

YANG Xiang-Jun,MA Zhi-Gang,WEI Qun-Yan,HUANG Zhang-Jie,CHEN Jing

2007-01-01

Abstract:Ultrafine powder of spinel type ferrite Ni_0.6 Cu_0.2 Zn_0.2 Fe_2O_4 was prepared from Fe(NO_3)_3·9H_2O, Ni(NO_3)_2·6H_2O,Zn(NO_3)_2·6H_2O,Cu(NO_3)_2·3H_2O and citric acid via solid state reaction at low heating temperatures.The reaction mechanism and structure of the product were investigated by means of FT-IR,DTA-TG,XRD,TEM and SEM.The FT-IR results show that the metal ions could react with citric acid by grinding for 30 min,and the carboxyl groups of the citric acid were coordinated to the metal ions in a monodentate fashion.The XRD and FT-IR analyses for the samples sintered at different temperatures indicate that the spinel crystal structure integrates gradually with the increase of the calcination temperature.Accor- ding to the calculation via the Scherrer formula and the TEM analysis,the particle size of the ferrite was about 30～40 nm after the dried gel was decomposed at 350℃for 1 h,and the particle size increased to 200～300 nm when the decomposed dried gel sample was sintered at 900℃for 2 h.