Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Microstructure and mechanical properties of ZrB2–MoSi2 ceramic composites produced by different sintering techniques

Properties of a Pressureless‐Sintered ZrB2–MoSi2 Ceramic Composite

Microstructure and Mechanical Properties of ZrB2-SiC Composites

Microstructures and mechanical properties of reactive spark plasma-sintered ZrB2–SiC–MoSi2 composites

Densification, microstructure and mechanical properties of ZrB2–SiCw ceramic composites

Microstructure and mechanical properties of ZrB2–SiC nanocomposite ceramic

Microstructures and Mechanical Properties of Hot-Pressed MoSi2–matrix Composites Reinforced with SiC and ZrO2 Particles

Preparation and Mechanical Properties of ZrB2-based Ceramics Using MoSi2 As Sintering Aids

Pressureless Sintering of Zrb2-Sic Composites Strengthening by Ultra-Fine Ceramic Powders

Preparation and Mechanical Properties of Laminated Zirconium Diboride/molybdenum Composites Sintered by Spark Plasma Sintering

Microstructure and mechanical properties of hot pressed ZrC-SiC-ZrB 2 composites

Effects of SiC Platelet and ZrSi2 Additive on Sintering and Mechanical Properties of ZrB2-based Ceramics by Hot-Pressing

Microstructure and Mechanical Properties of ZrB2–SiC Composites Prepared by Gelcasting and Pressureless Sintering

Microstructure and Properties of an Electroconductive SiC-based Composite

Microstructure and Mechanical Properties of Hot-Pressed Al2O3–mullite–ZrO2–SiC Composites

Pressureless Sintering of High‐Density ZrB2–SiC Ceramic Composites

Microstructure and mechanical properties of zirconia-toughened ZrB2–MoSi2 composites prepared by hot-pressing

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

MoSi2–ZrO2 composites—fabrication, microstructures and properties