Depressing effect of 0.1wt.% Cr addition into Sn–9Zn solder alloy on the intermetallic growth with Cu substrate during isothermal aging

Jin Hu,Anmin Hu,Ming Li,Dali Mao
DOI: https://doi.org/10.1016/j.matchar.2009.12.019
IF: 4.537
2010-01-01
Materials Characterization
Abstract:In this paper, the effect of 0.1wt.% Cr addition into Sn–9Zn lead-free solder alloys on the growth of intermetallic compound (IMC) with Cu substrate during soldering and subsequent isothermal aging was investigated. During soldering, it was found that 0.1wt.% Cr addition did not contribute to forming the IMC, which was verified as the same phase structure as the IMC for Sn–9Zn/Cu. However, during solid-state isothermal aging, the IMC growth was remarkably depressed by 0.1wt.% Cr addition in the Sn–9Zn solder, and this effect tended to be more prominent at higher aging temperature. The activation energy for IMC growth was determined as 21.2kJmol−1 and 42.9kJmol−1 for Sn–9Zn/Cu and Sn–9Zn–Cr/Cu, respectively. The reduced diffusion coefficient was confirmed for the 0.1Cr-containing solder/Cu. Energy-dispersive X-ray mapping and point analysis also showed ZnCr phase existing in solder matrix, which can reduce diffusion rate of Zn atoms.
What problem does this paper attempt to address?