Abstract:Porous hollow silica particles possess promising applications in many fields, ranging from drug delivery to catalysis. From the synthesis perspective, the most challenging parameters are the monodispersity of the size distribution and the thickness and porosity of the shell of the particles. This paper demonstrates a facile two-pot approach to prepare monodisperse porous-hollow silica particles with uniform spherical shape and well-tuned shell thickness. In this method, a series of porous-hollow inorganic and organic-inorganic core-shell silica particles were synthesized via hydrolysis and condensation of 1,2-bis(triethoxysilyl) ethane (BTEE) and tetraethyl orthosilicate (TEOS) in the presence of hexadecyltrimethylammonium bromide (CTAB) as a structure-directing agent on solid silica spheres as core templates. Finally, the core templates were removed via hydrothermal treatment under alkaline conditions. Transmission electron microscopy (TEM) was used to characterize the particles′ morphology and size distribution, while the changes in the chemical composition during synthesis were followed by Fourier-transform infrared spectroscopy. Single-particle inductively coupled plasma mass spectrometry (spICP-MS) was applied to assess the monodispersity of the hollow particles prepared with different reaction parameters. We found that the presence of BTEE is key to obtaining a well-defined shell structure, and the increase in the concentration of the precursor and the surfactant increases the thickness of the shell. TEM and spICP-MS measurements revealed that fused particles are also formed under suboptimal reaction parameters, causing the broadening of the size distribution, which can be preceded by using appropriate concentrations of BTEE, CTAB, and ammonia.

Polyelectrolyte Controlled Large-Scale Synthesis of Hollow Silica Spheres with Tunable Sizes and Wall Thicknesses

Synthesis of siliceous hollow spheres with large mesopore wall structure by supercritical CO2-in-water interface templating.

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents

Synthesis and Morphology Control of Hollow Silica Spheres

Template Polymerization Based on Stober Method: an Improved Method for Fabrication of Hollow Polysiloxane Spheres

Facile Large-Scale Synthesis Of Monodisperse Mesoporous Silica Nanospheres With Tunable Pore Structure

Composite nanospheres of PAA/silica controlled by anionic polymer

Synthesis of uniform-size hollow silica microspheres through interfacial polymerization in monodisperse water-in-oil droplets

Mesostructure-tunable and size-controllable hierarchical porous silica nanospheres synthesized by aldehyde-modified Stöber method

Fabrication of Teardrop-Shaped Silica Particles in Polyelectrolyte Diluted Solution Through in Situ Sol–gel Process

Synthesis of Porous Hollow Organosilica Particles with Tunable Shell Thickness

Size-Controllable Synthesis of Worm-Like Sio2 Microspheres Using Dodecylamine As Direct Agent in Ethanol/Water Solvent System

Facile fabrication of hollow mesoporous silica microspheres with hierarchical shell structure via a sol–gel process

Synthesis of micrometer-sized hard silica spheres with uniform mesopore size and textural pores

Facile synthesis of hollow silica microspheres

Synthesis of Monodisperse Silica Microspheres with Solid Core and Mesopore Shell

Synthesis of Silica Hollow Spheres with Diameter Around 50 Nm by Anionic Surfactant

A Simple and Low-Cost Method for the Preparation of Monodisperse Hollow Silica Spheres

Synthesis of Ordered Mesoporous Silica Spheres with Controllable Diameter in Micrometer

Synthesis of Ordered Mesoporous Silica with Tunable Morphologies and Pore Sizes Via a Nonpolar Solvent-Assisted Stöber Method

A new ‘pH-induced rapid colloid aggregation’ method to prepare micrometer-sized spheres of mesostructured silica in water-in-oil emulsion