Abstract:Hollow silica nanospheres with mesoporous shells were successfully fabricated with a new one-pot strategy by using a thermosensitive polymer, poly(N-isopropylacrylamide) (PNIPAm), as a reversible template without the need of further calcination or chemical etching. By simply regulating the solution temperature with respect to the lower critical Solution temperature (LCST) of PNIPAm, PNIPAm chains can reversibly form aggregates or dissolve in aqueous solution. The thermosensitive character makes PNIPAm chains behave as soft templates for the formation of core-shell silica nanospheres at elevated temperature (> LCST), and they will then diffuse out Of the cores at lower temperature (< LCST), leading to the formation of hollow silica nanospheres. The TEM, SEM, XRD, and N-2 adsorption-desorption results indicate that the shells of such hollow silica nanospheres also contain large quantities of irregular mesopores. This new strategy was also tested with another thermosensitive polymer, poly(vinyl methyl ether) (PVME). However, only solid silica nanospheres with a broad size distribution were obtained when PVME was used. We speculated on the possible formation mechanism of hollow silica nanospheres with PNIPAm templates. The effects of the initial concentration of PNIPAm, the molecular weight of PNIPAm, and the pretreatment of silica precursor on the morphology and size of the resultant hollow silica nanospheres were also investigated. The PNIPAm soft templates were confirmed to be recyclable.

Template Polymerization Based on Stober Method: an Improved Method for Fabrication of Hollow Polysiloxane Spheres

Template Polymerization-Solvent Extraction: A New Method For Fabrication Of Hollow Polysiloxane Particles

A Method for the Fabrication of Monodisperse Hollow Silica Spheres

A novel templating synthesis method for hollow polysiloxane micro capsules

Polyelectrolyte Controlled Large-Scale Synthesis of Hollow Silica Spheres with Tunable Sizes and Wall Thicknesses

Quaternized Polystyrene Composite Hollow Particles

Synthesis of polymer-silica hybrid microparticles with defined geometry using surface initiated atom transfer radical polymerization

Fabrication of Hollow Silica Spheres Using Droplet Templates Derived from a Miniemulsion Technique.

Novel and feasible method for synthesis of monodispersed hollow silicon dioxide submicrospheres

Studies on Template Synthesis Method for Fabrication of Hollow Microcapsules from Diphenyldimethoxysilane Monomer

Synthesis of siliceous hollow spheres with large mesopore wall structure by supercritical CO2-in-water interface templating.

Template Synthesis of Hydrogel Composite Hollow Spheres Against Polymeric Hollow Latex

A Novel Method for the Fabrication of Monodisperse Hollow Silica Spheres

Facile Fabrication Method And Characterization Of Hollow Ag/Sio2 Double-Shelled Spheres

A novel approach for preparation of “cage-like” multihollow polymer microspheres through sulfonated polystyrene particles

Template synthesis of composite hollow spheres using sulfonated polystyrene hollow spheres

One-Pot Preparation of Hollow Silica Spheres by Using Thermosensitive Poly(N-Isopropylacrylamide) As A Reversible Template

Influence of preparation method on the morphology of voided SiO2 microspheres prepared by template process

Inward Template Synthesis of Intact Hollow Spheres

Facile Fabrication of Carbon Spheres with Tunable Morphologies from Novel Polymeric Carbon Precursors.

Fabrication of Porous Silica Microspheres under the Assistance of Solid Template