Abstract:Crystalline NiCX nanorods (NCNRs) were successfully prepared on fused silica and sapphire (0001) substrates with different shapes and growth orientations via the pulsed laser deposition accompanied by N-2 annealing. The effects of experimental parameters including substrates, annealing duration, temperature and environment on the growth of crystalline NCNRs were studied in detail. Densely and uniformly distributed NCNRs with varied crystal orientations of hexagonal structure could be grown on silica and sapphire substrates, and only groups of SiO2 nanowires were grown on Si substrates. The NCNRs can be formed within only 3 min in pure N-2 atmosphere at the annealing temperature of 1200 degrees C. It was found that the pure N-2 atmosphere in the annealing process was necessary for the NCNR growth and the annealing in air could only obtain sparsely distributed nano-scaled particles. Besides, the NCNR films demonstrated excellent transmittance in visible light. (C) 2017 Elsevier B.V. All rights reserved.

Solvothermal Growth of Nis Single-Crystalline Nanorods

Ultrafast growth of single-crystalline Si nanowires

Solution-phase synthesis of nickel phosphide single-crystalline nanowires

Single crystalline CdS nanorods fabricated by a novel hydrothermal method

Growth of Crystalline Sb2S3 Nanorods by Hydrothermal Method

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

A Novel Hydrothermal Synthesis of Single Crystalline Pbs Nanorods and Their Characterization

Synthesis of Single Crystalline CdS Nanorods by a PVP-assisted Solvothermal Method

Synthesis of NiO nanowires by a sol-gel process

Preparation And Characterization Of Bismuth Sulfide Single Crystal Nanorods In Ionic Liquids

Formation Process of Cds Nanorods Via Solvothermal Route

Synthesis of Single-Crystalline NiCx Nanorods by Pulsed Laser Deposition Accompanied by N2 Annealing

Synthesis and Characterization of Ni(OH)2 Single-crystal Nanorods

Synthesis of NiO nanorods by a novel simple precursor thermal decomposition approach

Solvothermal Synthesis to Nie2 (E = Se, Te) Nanorods at Low Temperature

Syntheses, Growth Mechanism, and Optical Properties of [001] Growing Bi2S3 Nanorods

Synthesis and Characterization of Mn2P2S6 Single-Crystal Nanorods and Nanotubes.

Synthesis of Novel Sbsi Nanorods by A Hydrothermal Method

Effects of the Experimental Conditions on the Growth of Crystalline Nicx Nanorods Via Pulsed Laser Deposition Accompanied by N-2 Annealing

Hydrothermal Synthesis of Flower-Like Bi2S3with Nanorods in the Diameter Region of 30 Nm

Pii: s0025-5408(01)00734-6