Abstract:A series of nickel selenides (NiSe2 microcrystals, Ni1-xSe and Ni3Se2 microspheres) has been successfully synthesized through a convenient, low-temperature hydrothermal method. A good nucleation and growth environment has been created by forming a uniform and transparent solution reaction system. The compositions (including the x value of Ni1-xSe), phase structures, as well as the morphologies of nickel selenides, can be controlled by adjusting the Ni/Se ratio of the raw materials, the pH, the reaction temperatures and times, and so forth. The newly produced Se microspheres in the system have been used as both reactant and in situ template to the Ni1-xSe microspheres. It is found that Ni1-xSe microspheres act as the intermediate precursor during the formation of Ni3Se2 microspheres. Under certain conditions, hexagonal NiSe microspheres can be converted into rhombohedral NiSe nanowires in solution. The formation mechanisms of a series of nickel selenides has been investigated in detail by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses. This work has provided a general, simple, and effective method to control the composition, phase structure, and morphology of metal selenides in aqueous solution, which will be important for inorganic synthesis methodology and further applications of selenides.

Solvothermal Synthesis to Nie2 (E = Se, Te) Nanorods at Low Temperature

A Hydrothermal Method for Low-Temperature Growth of Nanocrystalline Pyrite Nickel Diselenide

Synthesis of nanocrystalline lead chalcogenides PbE (E = S, Se, or Te) from alkaline aqueous solutions

Solvothermal route to Bi3Se4 nanorods at low temperature

A direct solvothermal route to nanocrystalline selenides at low temperature

Solvothermal Route to Cote2 Nanorods

Solvothermal Synthesis to Cu2snse4 Nanocrystals at Low Temperature

Elemental Solvothermal Reaction to Produce Ternary Semiconductor CuInE2 (E = S, Se) Nanorods.

High-Density Se Nanoneedles Having No Catalyst Tips Quasi-Vertically Grown on Quartz Substrates Via Destructive Thermal Evaporation

A solvothermal synthetic route to CdE (E = S, Se) semiconductor nanocrystalline

Controllable Growth of Se Nanotubes and Nanowires from Different Solvent During the Sonochemical Process

Synthesis of Nanocrystalline Cobalt Selenide in Nonaqueous Solvent

Selenium Nanotubes Synthesized by A Novel Solution Phase Approach

Solvothermal Growth of Nis Single-Crystalline Nanorods

Controlled Hydrothermal Synthesis and Structural Characterization of A Nickel Selenide Series

Solvothermal Elemental Direct Reaction to Cde (E = S, Se, Te) Semiconductor Nanorod

Room temperature synthesis of single-crystal Te nanorods from Na2TeO4

Synthesis and Characterization of Nanocrystalline Bi2Se3 by Solvothermal Method

A Simple Synthetic Method for MSe2 (m=fe, Co or Ni) Nanocrystallites at Low Temperature

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

Solvothermal Route to Nanocrystalline CdSe