Preparation and electrochemical characterization of an activated carbon material of high specific surface area for supercapacitor

LI Jing,LAI Yan-qing,LI Jie,Liu Ye-xiang

DOI: https://doi.org/10.3969/j.issn.1671-6620.2008.01.008

2008-01-01

Abstract:A low-cost organic compound comprising mainly polyarylate was selected as precursor and a chemical activation method was used to prepare an activated carbon material of large surface area,with which the activated carbon electrodes of high specific capacitance were fabricated for supercapacitor.The effect of activating temperature on the specific capacitance of activated carbon electrode was studied.The relationship between the pore structure,surface area and specific capacitance of activated carbon electrode were discussed.The electrochemical characterization was also conducted with cyclic voltammetry and AC impedance methods.The results showed that,in the range of 500 ℃ to 700 ℃,the specific capacitance of activated carbon electrodes obviously increased with the increase of activation temperature.When the activation temperature is above 700 ℃,the specific capacitance of activated carbon changes little with further increase of activation temperature.The activated carbon prepared at 700 ℃ had obvious porous structure,and its pore volume and surface area were 1.038 cm3/g and 1 959 m2/g,respectively.The electrode fabricated with the activated carbon prepared at 700 ℃ exhibited a high specific capacitance of 211 F/g at a charge-discharge current of 10 mA/cm2,an ESR(equivalent series resistance) of about 0.9 Ω/cm2,a residual capacitance more than 90% after 500 cycles.A pure capacitance behavior can be found at the frequency below the knee in its AC impedance spectroscopy.Its cyclic voltammetry curve shows good reversibility.