Abstract:Most carbon electrode materials for supercapacitors (SCs) are prepared by the conventional KOH activation method that entails several steps at higher temperatures resulting in low‐energy density. Herein, we report one‐step facile carbonization and low‐concentration‐activation aided synthesis of activated carbon (AC) from Prunus dulcis (almond) peel (AP) by using three activating agents, namely (a) KOH (AC‐K1); (b) KOH with K3[Fe(CN)6] (AC‐K2); (c) KOH with K3[Fe(CN)6] and K4[Fe(CN)6] (AC‐K3) for high‐performance symmetric supercapacitor (SSCs) applications in 6 M KOH and 1 M TEABF4 electrolytes. Detailed structural and chemical characterization studies were performed on the as‐prepared AC‐K1/K2/K3 samples and optimization studies revealed that AC‐K3 electrode delivers the highest performance due to the presence of trace amount of iron salts in the carbon network that acts as a catalyst and induces fast charge‐transfer for electrochemical reactions. The BET surface area of AC‐K1, AC‐K2, and AC‐K3 are found to be 408.89 m2 g−1, 819.79 m2 g−1, and 1061.6 m2 g−1, respectively. AC‐K3 electrode delivers an outstanding half‐cell specific capacitance of 320 F g−1 at 1 A g−1 in 6 M KOH. The SC device with AC‐K3 electrode delivers full‐cell specific capacitance of 290 F g−1 and 370.37 F g−1 in 6 M KOH and 1 M TEABF4, respectively. The highest energy density of 41.24 Wh kg−1 at 1349 W kg−1 power with the extended potential of ~2.7 V is delivered by the AC‐K3 electrode in 1 M TEABF4, which is considerably higher and unprecedented compared to other reported carbon materials. After 10 000 cycles, there is a ~100% capacitance retention. As a result of this study, the abundant bio‐derived AC‐K3 is found to be a potential long‐term electrode material for high‐energy SC applications. Almond peel derived iron‐induced activated carbon for supercapacitor in organic electrolyte.

Activated‐carbon‐based supercapacitors with high gravimetric‐ and volumetric capacitance at commercial‐level mass loading

Control of Nano Grains and Wide Carbocyclic Layer Space of Forming Active Carbon with Extraordinary Capacitance Characteristics in Supercapacitors

High‐performance activated carbons for supercapacitor: Effects of porous structures, heteroatom doping, and morphology

High-performance supercapacitor electrode at commercial-level mass loading from N-enriched activated carbon derived from soybean dregs

Filling Macro/mesoporosity of Commercial Activated Carbon Enables Superior Volumetric Supercapacitor Performances

Boosting Supercapacitive Performance of Flexible Carbon Via Surface Engineering.

A high-performance supercapacitor based on activated carbon fibers with an optimized pore structure and oxygen-containing functional groups

Cu-modified biomass-derived activated carbons for high performance supercapacitors

Synthesis of activated carbon nanospheres with hierarchical porous structure for high volumetric performance supercapacitors

Biobased Nano Porous Active Carbon Fibers for High-Performance Supercapacitors

Electrochemical Performance of Chemically Activated Carbons from Sawdust as Supercapacitor Electrodes

Enhancing the pore wettability of coal-based porous carbon as electrode materials for high performance supercapacitors

Regulating the properties of activated carbon for supercapacitors: impact of particle size and degree of aromatization of hydrochar

Enabling high surface and space utilization of activated carbon for supercapacitors by homogeneous activation

Synthesis of O-doped coal-based carbon electrode materials by ultrasound-assisted bimetallic activation for application in supercapacitors

A High‐Performance Symmetric Supercapacitor from Porous Activated Carbon under Compression

Controlling and optimizing the morphology and microstructure of 3D interconnected activated carbons for high performance supercapacitors

Corncob-Derived Activated Carbon as Electrode Material for High-Performance Supercapacitor

Honeycombed activated carbon with greatly increased specific surface by direct activation of glucose for supercapacitors

Performance of activated carbons synthesized from fruit dehydration biowastes for supercapacitor applications

Almond peel‐derived iron‐induced activated carbon for high energy and long‐life supercapacitor in organic electrolyte