Abstract:A low-cost organic compound comprising mainly polyarylate was selected as precursor and a chemical activation method was used to prepare an activated carbon material of large surface area,with which the activated carbon electrodes of high specific capacitance were fabricated for supercapacitor.The effect of activating temperature on the specific capacitance of activated carbon electrode was studied.The relationship between the pore structure,surface area and specific capacitance of activated carbon electrode were discussed.The electrochemical characterization was also conducted with cyclic voltammetry and AC impedance methods.The results showed that,in the range of 500 ℃ to 700 ℃,the specific capacitance of activated carbon electrodes obviously increased with the increase of activation temperature.When the activation temperature is above 700 ℃,the specific capacitance of activated carbon changes little with further increase of activation temperature.The activated carbon prepared at 700 ℃ had obvious porous structure,and its pore volume and surface area were 1.038 cm3/g and 1 959 m2/g,respectively.The electrode fabricated with the activated carbon prepared at 700 ℃ exhibited a high specific capacitance of 211 F/g at a charge-discharge current of 10 mA/cm2,an ESR(equivalent series resistance) of about 0.9 Ω/cm2,a residual capacitance more than 90% after 500 cycles.A pure capacitance behavior can be found at the frequency below the knee in its AC impedance spectroscopy.Its cyclic voltammetry curve shows good reversibility.

Large-surface-area activated carbon with high density by electrostatic densification for supercapacitor electrodes

Amine-enriched Graphene Quantum Dots for High-pseudocapacitance Supercapacitors

Control of Nano Grains and Wide Carbocyclic Layer Space of Forming Active Carbon with Extraordinary Capacitance Characteristics in Supercapacitors

Boosting the Energy Storage Densities of Supercapacitors by Incorporating N-doped Graphene Quantum Dots into Cubic Porous Carbon

Ion Intercalation into Graphitic Carbon with a Low Surface Area for High Energy Density Supercapacitors

Ultrafast pore-tailoring of dense microporous carbon for high volumetric performance supercapacitors in organic electrolyte

Preparation and electrochemical characterization of an activated carbon material of high specific surface area for supercapacitor

Freestanding biomass‐derived and self‐doped carbon electrodes with high loading for high‐performance supercapacitors

Chitin derived nitrogen-doped porous carbons with ultrahigh specific surface area and tailored hierarchical porosity for high performance supercapacitors

Graphene Quantum Dot Reinforced Electrospun Carbon Nanofiber Fabrics with High Surface Area for Ultrahigh Rate Supercapacitors

Enabling high surface and space utilization of activated carbon for supercapacitors by homogeneous activation

Self-supported nickel cobalt carbonate hydroxide nanowires encapsulated cathodically expanded graphite paper for supercapacitor electrodes

Balanced Energy Density and Power Density: Asymmetric Supercapacitor Based on Activated Fullerene Carbon Soot Anode and Graphene-Co3o4 Composite Cathode

Ultramicroporous Carbons Puzzled by Graphene Quantum Dots: Integrated High Gravimetric, Volumetric, and Areal Capacitances for Supercapacitors

Ultrathin Carbon Gauze for High-Rate Supercapacitor

Optimized Mesopores Enabling Enhanced Rate Performance in Novel Ultrahigh Surface Area Meso-/Microporous Carbon for Supercapacitors

Capacitive Performance of a Heteroatom-Enriched Activated Carbon in Concentrated Sulfuric Acid

Packing Activated Carbons into Dense Graphene Network by Capillarity for High Volumetric Performance Supercapacitors

Design and structure optimization of 3D porous graphitic carbon nanosheets for high-performance supercapacitor

Three-dimensional activated graphite paper for high-performance supercapacitors

Controlling and optimizing the morphology and microstructure of 3D interconnected activated carbons for high performance supercapacitors