Synthesis of biomass-based porous graphitic carbon combining chemical treatment and hydrothermal carbonization as promising electrode materials for supercapacitors

Xiaochen Jiang,Feiqiang Guo,Xiaopeng Jia,Shuang Liang,Kuangye Peng,Lin Qian

DOI: https://doi.org/10.1007/s11581-020-03487-8

IF: 2.961

2020-02-10

Ionics

Abstract:<p class="a-plus-plus">A synthesis strategy was developed for preparing porous graphitic carbon with high electrochemical performance from peanut shell through chemical treatment by NH<sub class="a-plus-plus">4</sub>OH, HNO<sub class="a-plus-plus">3</sub>, and H<sub class="a-plus-plus">2</sub>SO<sub class="a-plus-plus">4</sub>, subsequent hydrothermal carbonization, and ZnCl<sub class="a-plus-plus">2</sub> activation under CO<sub class="a-plus-plus">2</sub> atmosphere. At a certain activation temperature of 700 °C, the carbon sample after NH<sub class="a-plus-plus">4</sub>OH pretreatment (NHAC-700) achieved the highest specific capacitance of 256.05 F/g at the current density of 0.5 A/g due to its high surface area and good pore size distribution. The porosity and electrochemical performance of NH<sub class="a-plus-plus">4</sub>OH-pretreated carbon was further improved by improving the activation temperature to 800 °C (NHAC-800). The NHAC-800 possessed a large surface area of 2129.5 m<sup class="a-plus-plus">2</sup>/g with a high proportion of mesopores in the pore size range of 2–5 nm. Electrochemical analysis in the three-electrode system showed that NHAC-800 electrode exhibited a high specific capacitance of 266.06 F/g at 0.5 A/g. In the two-electrode system, the symmetric supercapacitor assembled by NHAC-800 delivered an energy density of 32.08 Wh/kg at a power density of 1000 W/kg and maintained 25.63 Wh/kg at 20000 W/kg. NHAC-800 also displayed excellent cycle stability with the capacitance retention rate of 93.76% after 5000 cycles at a constant current density of 2 A/g.</p>

chemistry, physical,physics, condensed matter,electrochemistry