Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

Fabrication of Mo-Ti<sub>3</sub>SiC<sub>2</sub> Layered Material by Spark Plasma Sintering and its Interface Stability at 800°C

Synthesis, microstructure, and properties of high purity Mo2TiAlC2 ceramics fabricated by spark plasma sintering

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

Structural characterization and reaction mechanism of the Ti/SiC gradient material with Mg 2 Si additive fabricated by reaction sintering

Effect of temperature on the structure and mechanical properties of SiC–TiB2 composite ceramics by solid-phase spark plasma sintering

Preparation of Al2O3/Ti3SiC2 multilayer materials by in-situ synthesis

Fabrication of SiCAlN/Mo functionally gradient material for high temperature use

Enhanced Formation of the C54 Phase of Tisi2 by an Interposed Layer of Molybdenum

Fabrication of plasma-sprayed TiC-Ti5Si3-Ti3SiC2 composite coatings from the annealed Ti/SiC powders

High Temperature Oxidation Behavior of SiC Coating Materials

Theoretical analysis of Si3N4/TiC interfacial properties and material preparation

Microstructure Evolution of the Interface in SiCf/TiC-Ti3SiC2 Composite under Sequential Xe-He-H Ion Irradiation and Annealing Process

In Situ Synthesis of (Mo,Cr)Si2 Composites by Spark Plasma Sintering

Cold Sprayed Additive Manufacturing of SiC/Al Metal Matrix Composite: Synthesis, Microstructure, Heat Treatment and Tensile Properties

Tensile behavior of the designed SiCf/Ti2AlNb/Ti17 composites

Microstructure and Interfacial Strength of SiC Fiber-Reinforced Ti17 Alloy Composites with Different Consolidation Temperatures

In Situ Characterization of Titanium Silicide Formation: the Effect of Mo Interlayer, Temperature Ramp-Rate, and Annealing Atmosphere

Microstructure characterization and mechanical properties of in situ synthesized Ti2(Al,Si)C reinforced Al composites

Fabrication and Mechanical Properties of High-Pure Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials Directly by Hot-Pressing its Powder

Machinable and mechanical properties of sintered Al 2 O 3 -Ti 3 SiC 2 composites

Effect of spark plasma sintering temperature on the multi-scale microstructure evolution and mechanical properties of Ti 2 AlC/TiAl composites with network architecture