Abstract:The components made out of hypereutectic high-chromium cast iron (HCCI), featured with high abrasion resistance and hardness, are usually subjected to destabilization treatment before use, to improve their hardness and wear resistance by destabilizing the retained austenite which transforms to martensite. This study investigates the effects of destabilization and tempering heat treatment on the microstructure and mechanical properties of an HCCI with and without modification of primary carbides. For the unmodified HCCI, the destabilization simultaneously increased both hardness and the transverse rupture strength (TRS). Increasing the destabilization temperature from 970 to 1090 °C led to a marginal decrease in hardness and slight increase in TRS. Destabilization at 1090 °C increased the transverse rupture strength (TRS) by 54% compared to the as-cast HCCI without reduction in wear resistance due to the coarsening of the secondary carbides. In addition, tempering within a temperature range from 200 to 280 °C after destabilization at 1090 °C led to a slight decrease in hardness, but an increase in TRS and wear resistance. Further increasing the tempering temperature to 310, 340 and 400 °C did not vary the properties. Tempering at 280 °C after destabilization at 1090 °C enabled more than 85% increase in TRS compared to the as-cast HCCI. The influence of destabilization temperature on the TiB 2 -modified HCCI is similar to the unmodified alloy. But, tempering after destabilization at 1090 °C decreased both hardness and TRS without significant variation of wear resistance even though a TRS peak was obtained at 310 °C tempering. Hence, to achieve the best performance an optimized heat treatment for the unmodified HCCI is destabilization at 1090 °C followed by tempering at 280 °C. For the TiB 2 -modified HCCI, tempering is not needed. Rationalizations of the mechanical properties are also discussed in terms of microstructure.

Effects of Heat Treatment on Hardening Behavior of 3Cr14Mn4B High Chromium Cast Iron

Effect of quenching temperature on microstructure and properties of multivariate high chromium cast iron

Microscopic Study of Carbide Precipitation during Heat Treatment of 35Cr–4C High Chromium Cast Iron

Effect of Chromium Content on Heat Treatment Behavior of Multi-Alloyed White Cast Iron for Abrasive Wear Resistance

Characterization of Microstructure and Mechanical Properties of High Chromium Cast Irons Using Sem and Nanoindentation

Effect of Carbon and Cooling Rate on the Structure of Hypereutectic High Chromium Cast Iron in the Cast State and after Heat Treatment

Wear Behavior and Microstructure Changes of a High Chromium Cast Iron: The Combined Effect of Heat Treatment and Alloying Elements

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

Effects of traditional heat treatment and a novel deep cryogenic treatment on microstructure and mechanical properties of low-carbon high-alloy martensitic bearing steel

Influence of Cooling Rate After Destabilization on Microstructure and Hardness of a High-Cr Cast Iron

Effects of annealing treatment on microstructure and hardness in the 28 wt% Cr cast iron with Mo/W addition

Tempering temperature dependence on the microstructure, mechanical properties and wear behaviour of a novel high chromium cast iron

Influence of Heat Treatment on Erosive Wear Resistance of High Cr Cast Irons

Effects of Heat Treatment Process on Microstructure and Mechanical Properties for Extra-Thick High-Strength Steel Plate

Effect of tempering temperature on microstructure and properties of low silicon hypereutectic high chromium cast ironAuswirkung der Anlasstemperatur auf das Gefüge und die Eigenschaften von übereutektischem Gusseisen mit niedrigem Siliziumgehalt und hohem Chromgehalt

Effect of Chromium on Microstructure and Properties of High Boron White Cast Iron

Effects of Manganese and Heat Treatment on Mechanical Properties in Spheroidal Graphite Cast Iron

Heat Treatment Effect on the Microstructure and Tribological Behaviour of a High Chromium Cast Iron with 0.5% of Niobium

Microstructure and Mechanical Properties of High Boron White Cast Iron with about 4 Wt% Chromium

Effects of Heat Treatment on Microstructure and Impact Resistance of High Manganese Steels

Effects of destabilization and tempering on microstructure and mechanical properties of a hypereutectic high-chromium cast iron