Abstract:Porous electric double-layer capacitors were prepared successfully with acetylene black and PTFE, where acetylene black was used as electrode precursor and PTFE as a binding. The acetylene powder and the electrode microstructure were measured by both TEM and SEM respectively. The charge-and-discharge curves were measured using a charge/discharge meter. In conclusion, the specific capacitance of the double-layer capacitors increased with the decrease in preparation pressure of the electrode due to increasing both the proportion of the effective micro-pores and the available surface. As the preparation pressure decreased from 48MPa to 16MPa, 17% of the specific capacitance was increased. However, when the pressure was above 48MPa, the capacitance had almost no change with decreasing preparation pressure because the pressure affected hardly on available surface. Moreover, the specific capacitance increased with decreasing PTFE binding due to the increase in available surface. 46% of the specific capacitance was actively ascended as PTFE decreased from 14% to 6%. In addition, the charge density increased, hence the chargeable voltage increased with the increase in available surface because of high preparation pressure. Likewise, the charge density might increase and the chargeable voltage then increased with the increase in concentration of the electrolyte. Both the charge and the discharge behaviors of the double-layer capacitor were directly related to both the distribution and size of electrode pores. The capacitor discharge slowly first and then speedily while the proportion of the micro-pores increased with increasing preparation pressure.

Preparing technique optimization and performance of double-layer capacitor

Fabrication and Properties of Double-layer Capacitor with Acetylene Black Electrode

Preparation and Electrochemical Properties of PF-based Activated Carbon

Performance of Electric Double Layer Capacitors Using Active Carbons Prepared from Petroleum Coke by Koh and Vapor Re-Etching

Control of Nano Grains and Wide Carbocyclic Layer Space of Forming Active Carbon with Extraordinary Capacitance Characteristics in Supercapacitors

Porous carbon with tailored pore size for electric double layer capacitors application

Boosting Supercapacitive Performance of Flexible Carbon Via Surface Engineering.

Preparation and Application of Electrochemical Double Layer Capacitor

Preparation of layered-porous carbon from coal tar pitch narrow fractions by single-solvent extraction for superior cycling stability electric double layer capacitor application

The Effect of Pre-Carbonization of Mesophase Pitch-Based Activated Carbons on Their Electrochemical Performance for Electric Double-Layer Capacitors

Preparation of Mesophase-Pitch-based Activated Carbons for Electric Double Layer Capacitors with High Energy Density

Oxygen-rich Hierarchical Porous Carbon Derived from Coal Tar Pitch for Superior Electric Double Layer Capacitor Application

Superior capacitive storage behavior of porous carbon electrode with high mass loading

Biomass-derived nitrogen and sulfur co-doped sheet-like porous carbon for high-performance supercapacitors

Tuning pore structure of polymer-derived carbon materials for supercapacitor electrode materials using microscopic phase separation engineering

Coupling of reasonable micro-defect structure and multiple chemisorption sites for boosting the K + storage capacity in dual-carbon potassium ion hybrid capacitors

High-Performance Supercapacitors Based on Graphene/Activated Carbon Hybrid Electrodes Prepared Via Dry Processing

Regulation of the mesopore proportion of porous carbon for optimizing the performance of electric double layer capacitors

A novel two-prong strategy to boost the capacitive performance of commercial carbon cloth

Preparation of Advanced Multi-Porous Carbon Nanofibers for High-Performance Capacitive Electrodes in Supercapacitors

Cistanches herba residues derived nitrogen and oxygen self-doped porous carbon for high performance supercapacitor