Abstract:This paper reports the synthesis of semiconductor nanocrystals of PbS through a facile and inexpensive synthetic route between lead acetate [Pb(Ac)2·3H2O] and dithioglycol (HSCH2CH2SH) without any surfactant. The products were characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), Raman spectroscopy, x-ray photelectron spectroscopy (XPS) and infrared (IR) spectroscopy. The size of cube-shaped PbS nanocrystals can be controlled by changing the relative amount of Pb(Ac)2·3H2O and dithioglycol. Smaller cube-shaped PbS nanocrystals were obtained at higher sulfur content in the reaction system. The nanometre-sized single crystals of PbS measure ~83 nm × 59 nm × 22 nm and 39 nm × 10 nm × 7 nm, for lead acetate:dithioglycol ratios of 1:0.375 (denoted as PbS-1) and 1:1.5 (denoted as PbS-2), respectively, when a mixture of NaOH solution of lead acetate and ethyl alcohol solution of dithioglycol is maintained at 220 °C for 4 h in a Teflon-lined autoclave. XRD patterns and HRTEM images confirm the crystalline structure of the PbS crystals. TEM helped to determine the dimension of the single crystals. Raman, XPS and IR helped to further demonstrate the purity of the as-synthesized samples. The optical absorption spectra of suspensions of the these crystals in glycol show shifts in absorption band edge for as-prepared sample PbS-1 from 246 to 271 nm and for PbS-2 from 246 to 275 nm, after four days of storage, respectively. The photoluminescence peaks from the two samples are located at 434 and 433 nm for photoexcitation radiation of 315–355 nm, thus exhibiting a Stokes shift compared with band edge energy. The principal contribution of this work is that the nanometre-size PbS single crystals are prepared without using a surfactant or templating agent. The formation of a five-membered ring via the chelation between the Pb2+ ion and dithioglycol is considered to be crucial in this mechanism.

Synthesis of closed PbS nanowires with regular geometric morphologiesElectronic supplementary information (ESI) available: XRD pattern of the PbS CNWs, FTIR spectrum of the polymer, TEM images of more PbS CNWs. See http://www.rsc.org/suppdata/jm/b1/b111187f/

Novel single-crystal PbS nanowires directed by [200]

Synthesis Of Lead Sulfide/(Polyvinyl Acetate) Nanocomposites With Controllable Morphology

Synthesis of Pbs Nanoparticles in Polymer Matrices

A Novel Hydrothermal Synthesis of Single Crystalline Pbs Nanorods and Their Characterization

L-Cysteine-Assisted Tunable Synthesis of PbS of Various Morphologies

Synthesis and Formation Mechanism of PbCl2 Nanowires by Micelle-template Method

Synthesis and the Growth Mechanism of PbS Nanorod

Room Temperature Synthesis of PbS Nanocrystals with Different Morphologies in PEO–PPO–PEO Triblock Copolymers

Multi-morphology PbS: frame–film structures, twin nanorods, and single-crystal films prepared by a polymer-assisted solvothermal method

Growth and photoluminescence properties of PbS nanocubes

Synthesis and Growth Mechanism of Selenium Nanowire Bundles Via a Polymer-Controlled Chemical Route.

Growth of PbS crystals from nanocubes to eight-horn-shaped dendrites through a complex synthetic route

Ultrasound-assisted synthesis of PbS quantum dots stabilized by 1,2-benzenedimethanethiol and attachment to single-walled carbon nanotubes

Templated Synthesis of Cds/Pan Composite Nanowires under Ambient Conditions

Synthesis and characterization of PbS/modified hyperbranched polyester nanocomposite hollow spheres at room temperature

Synthesis and evolution of PbS nanocrystals through a surfactant-assisted solvothermal route.

Preparation of Star-Shaped Dendritic PbS Nanocrystals

Hierarchical, Star-Shaped Pbs Crystals Formed by A Simple Solution Route

Flowerlike Pbs Microcrystals: Citric Acid Assisted Synthesis, Shape Evolution, and Electrical Conductivities

Facile synthesis of PbS truncated octahedron crystals with high symmetry and their large-scale assembly into regular patterns by a simple solution route.