Abstract:This paper reports the synthesis of semiconductor nanocrystals of PbS through a facile and inexpensive synthetic route between lead acetate [Pb(Ac)2·3H2O] and dithioglycol (HSCH2CH2SH) without any surfactant. The products were characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), Raman spectroscopy, x-ray photelectron spectroscopy (XPS) and infrared (IR) spectroscopy. The size of cube-shaped PbS nanocrystals can be controlled by changing the relative amount of Pb(Ac)2·3H2O and dithioglycol. Smaller cube-shaped PbS nanocrystals were obtained at higher sulfur content in the reaction system. The nanometre-sized single crystals of PbS measure ~83 nm × 59 nm × 22 nm and 39 nm × 10 nm × 7 nm, for lead acetate:dithioglycol ratios of 1:0.375 (denoted as PbS-1) and 1:1.5 (denoted as PbS-2), respectively, when a mixture of NaOH solution of lead acetate and ethyl alcohol solution of dithioglycol is maintained at 220 °C for 4 h in a Teflon-lined autoclave. XRD patterns and HRTEM images confirm the crystalline structure of the PbS crystals. TEM helped to determine the dimension of the single crystals. Raman, XPS and IR helped to further demonstrate the purity of the as-synthesized samples. The optical absorption spectra of suspensions of the these crystals in glycol show shifts in absorption band edge for as-prepared sample PbS-1 from 246 to 271 nm and for PbS-2 from 246 to 275 nm, after four days of storage, respectively. The photoluminescence peaks from the two samples are located at 434 and 433 nm for photoexcitation radiation of 315–355 nm, thus exhibiting a Stokes shift compared with band edge energy. The principal contribution of this work is that the nanometre-size PbS single crystals are prepared without using a surfactant or templating agent. The formation of a five-membered ring via the chelation between the Pb2+ ion and dithioglycol is considered to be crucial in this mechanism.

Growth of PbS crystals from nanocubes to eight-horn-shaped dendrites through a complex synthetic route

HYDROTHERMAL SYNTHESIS OF DENDRITE-LIKE ZINC SULFIDE CRYSTALS

Hierarchical, Star-Shaped Pbs Crystals Formed by A Simple Solution Route

Synthesis and the Growth Mechanism of PbS Nanorod

Growth and photoluminescence properties of PbS nanocubes

Morphology Evolution Route of PbS Crystals Via Environment-Friendly Electrochemical Deposition

Surfactant‐Assisted Growth of Novel PbS Dendritic Nanostructures Via Facile Hydrothermal Process

Preparation of Star-Shaped Dendritic PbS Nanocrystals

Hydrothermal Synthesis, Characterization And Growth Mechanism Of Single Crystal Lead Titanate Pyrochlore Dendrites

Controlled Synthesis of PbWO4 Dendrites by a Simple Sonochemical Method

A Novel Hydrothermal Synthesis of Single Crystalline Pbs Nanorods and Their Characterization

Facile synthesis of PbS truncated octahedron crystals with high symmetry and their large-scale assembly into regular patterns by a simple solution route.

Shape-Controlled Syntheses of Pbs Submicro-/Nano-Crystals Via Hydrothermal Method

Novel single-crystal PbS nanowires directed by [200]

Synthesis and evolution of PbS nanocrystals through a surfactant-assisted solvothermal route.

L-Cysteine-Assisted Synthesis of PbS Nanocube-Based Pagoda-like Hierarchical Architectures

Synthesis and Characterization of Large-Scale Hierarchical Dendrites of Single-Crystal CdS

Shape Controllable Growth of PbS Polyhedral Crystals

Morphology Control of Pbs Nanocrystals by A Novel Hydrothermal Process

A novel aqueous-phase route to prepare flower-shaped PbS micron crystals

L-Cysteine-Assisted Self-Assembly of Complex Pbs Structures