Abstract:This paper reports the synthesis of semiconductor nanocrystals of PbS through a facile and inexpensive synthetic route between lead acetate [Pb(Ac)2·3H2O] and dithioglycol (HSCH2CH2SH) without any surfactant. The products were characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), Raman spectroscopy, x-ray photelectron spectroscopy (XPS) and infrared (IR) spectroscopy. The size of cube-shaped PbS nanocrystals can be controlled by changing the relative amount of Pb(Ac)2·3H2O and dithioglycol. Smaller cube-shaped PbS nanocrystals were obtained at higher sulfur content in the reaction system. The nanometre-sized single crystals of PbS measure ~83 nm × 59 nm × 22 nm and 39 nm × 10 nm × 7 nm, for lead acetate:dithioglycol ratios of 1:0.375 (denoted as PbS-1) and 1:1.5 (denoted as PbS-2), respectively, when a mixture of NaOH solution of lead acetate and ethyl alcohol solution of dithioglycol is maintained at 220 °C for 4 h in a Teflon-lined autoclave. XRD patterns and HRTEM images confirm the crystalline structure of the PbS crystals. TEM helped to determine the dimension of the single crystals. Raman, XPS and IR helped to further demonstrate the purity of the as-synthesized samples. The optical absorption spectra of suspensions of the these crystals in glycol show shifts in absorption band edge for as-prepared sample PbS-1 from 246 to 271 nm and for PbS-2 from 246 to 275 nm, after four days of storage, respectively. The photoluminescence peaks from the two samples are located at 434 and 433 nm for photoexcitation radiation of 315–355 nm, thus exhibiting a Stokes shift compared with band edge energy. The principal contribution of this work is that the nanometre-size PbS single crystals are prepared without using a surfactant or templating agent. The formation of a five-membered ring via the chelation between the Pb2+ ion and dithioglycol is considered to be crucial in this mechanism.

Synthesis and the Growth Mechanism of PbS Nanorod

Synthesis and evolution of PbS nanocrystals through a surfactant-assisted solvothermal route.

One-dimensional Growth of Rock-Salt PbS Nanocrystals Mediated by Surfactant/polymer Templates

Synthesis of Single-Crystal PbS Nanorods Via a Simple Hydrothermal Process Using PEO-PPO-PEO Triblock Copolymer As a Structure-Directing Agent.

Growth of single-crystal PbS nanorods via a biphasic solvothermal interface reaction route

Synthesis of Uniform PbS Nanorod Bundles Via a Surfactant-Assisted Interface Reaction Route

A Novel Hydrothermal Synthesis of Single Crystalline Pbs Nanorods and Their Characterization

Growth of PbS crystals from nanocubes to eight-horn-shaped dendrites through a complex synthetic route

Controlling Synthesis of PbS Nanostructures in Surfactant Solutions

PbS Assemblies: the Oriented Attachment of Individual PbS Nanocrystals

Preparation and Characterization of Oriented PbS Crystalline Nanorods in Polymer Films

Controllable Synthesis Of Pbse Nanostructures And Growth Mechanisms

Growth Mechanism And Properties Of Zno Nanorods Synthesized By Plasma-Enhanced Chemical Vapor Deposition

Growth of PbS architectural nanostructures catalyzed by silver nanocrystal seeds

Growth of Pbso4 Single-Crystal Nanorods and Optical Properties by A Microemulsion Approach

Controllable Growth of Silver-Seeded PbS Nanostructures

Controllable synthesis of PbSe nanorods via a low temperature solvothermal process

Novel single-crystal PbS nanowires directed by [200]

Shape-Controlled Synthesis and Related Growth Mechanism of Pb(OH) 2 Nanorods by Solution-Phase Reaction

Carbothermal reduction/sulfidation synthesis and structural characterization of PbS nanobelts and nanowires

Growth and photoluminescence properties of PbS nanocubes