Abstract:The Beam Dump Facility (BDF) is a planned fixed-target installation in CERN's North Area, set to start operating in 2031. A proton beam of 400 GeV/c will be delivered in 1 s pulses of 4e13 protons every 7.2 s, amounting to 4e19 protons on target (PoT) per year, with an average thermal power deposition of 305 kW. The experiment requires high-Z and high-density materials and involves challenging thermomechanical conditions; hence, a water-cooled refractory metal core is proposed. To prevent corrosion and erosion, the target materials - tungsten and a molybdenum-based alloy, TZM-, are clad with a tantalum alloy using hot isostatic pressing. To verify the reliability of the target design and manufacturing process, a reduced-scale prototype target was manufactured and irradiated with 2.4e16 PoT in 2018. This paper presents the findings of the post-irradiation examination (PIE) conducted 2.5 years later. The PIE consisted of non-destructive and destructive activities, including film imaging, microscopy, metrology, ultrasonic testing, microstructural analysis, and mechanical and thermal characterization. No irradiation effects resulting from thermal stresses, such as geometrical changes or cracks in the cladding, were observed, and it was determined that the bonding between the core and cladding materials was robust. Moreover, no changes were detected in the microstructures or mechanical properties of the bulk materials. In conclusion, the robustness of the target baseline design and manufacturing process was confirmed, validating its suitability for operating under the desired conditions. Nonetheless, the observed brittleness of sintered tungsten indicates a potential area for improvement to enhance the lifetime of the BDF target. Overall, the examinations provided valuable insights into the performance of the prototype and indicated potential refinements for the future BDF target complex.

Fabrication of a Tantalum-Clad Tungsten Target for KENS

R&D of a MW-class Solid-Target for a Spallation Neutron Source

Properties of Potassium Doped and Tantalum Containing Tungsten after Heavy Ion Irradiation

Technical Issues for the Fabrication of A Cn-Hccb-Tbm Based on Rafm Steel Clf-1

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

Exploring diffusion bonding of niobium and its alloys with tungsten and a molybdenum alloy for high-energy particle target applications

Development of resistant materials to beam impact and radiation damage

Study on the Edge-Cooling Target Structure for Transportable Accelerator-Driven Neutron Source

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

Development of a Neutron Generating Target for Compact Neutron Sources Using Low Energy Proton Beams

Post-irradiation examination of a prototype tantalum-clad target for the Beam Dump Facility at CERN

Strength Proof Evaluation of Diffusion-Jointed W/Ta Interfaces by Small Punch Test

Development of Advanced Materials for Spallation Neutron Sources and Radiation Damage Simulation Based on Multi-Scale Models

Development of irradiation tolerant tungsten alloys for high temperature nuclear applications

Comparative study of ITER conform tungsten grades exposed to high heat flux and neutron irradiation damage

Thermal–hydraulic Modeling and Transient Analysis of Helium-Cooled Tungsten Target Coupled with ADS Core

Accident Analysis of Tungsten Target Coupled with ADS Core

Post-Irradiation Examination of Commercial Tantalum Alloys Following Neutron Irradiation

Thermal Research of a Single Crystal Tungsten Target Positron Source for the STCF Project in China

Novel materials for next-generation accelerator target facilities

Multiphysics Simulations of Thermal Shock Testing of Nanofibrous High Power Targets