Abstract:Eu-doped (Y,Gd)BO_3∶Eu phosphor with spherical particle morphology, small size, high crystallinity and good photoluminescence (PL)intensity was prepared by co-precipitation method. Ultrafine precursor powders were obtained by controlling the solution concentration of Y~(3+),Gd~(3+),Eu~(3+) and temperature of system, the precursor is amorphous and soft when the system temperature maintain from 50 ℃ to 70 ℃. The phosphor particle size is influenced by the solution concentration, and the mean size of the (Y,Gd)BO_3∶Eu particles decreased from 2.3 μm to 0.8 μm when the solution concentration changed from 0.2 mol/L to (0.5) mol/L and shifted to the larger size with the further increase of the solution concentration. Conventional solid state (reaction) require higher sintering temperature above 1 200 ℃ for pure (Y,Gd)BO_3∶Eu phase. However, the co-(precipitation) allows a significant decrease of sintering temperature and the phosphor sintered at 800 ℃ have pure orthorborate phase already. The X-ray diffraction peak intensities increased with increasing temperature. The phosphors prepared at different temperature 800, 1 000, 1 200 and 1 300 ℃ were characterized by (X-ray) diffraction, SEM, particle size determination and photoluminescence. In addition, the characteristics of the particle were compared with those of a commercial product. Crystallinity,particle size and luminescence (intensity) are dependent on sintering temperature. The morphology and size of synthesized particles are strongly effected by sintering temperature. The phosphor particles prepared at 1 200 ℃ have the best (characteristics,) such as completely spherical shape, filled morphology, fine particle size, no-aggregation, and the commercial product prepared by conventional solid state reaction has a irregular shape with aggregation, the particles (began) to (agglomerate) and the particle size became larger at an firing temperature of 1 300 ℃. The (luminescence) intensities of the phosphors (increase) with the sintering temperature and the brightness of (phosphor) increase with increasing temperatures due to favorable crystallization and has a maximum values at (1 200 ℃) when excited with UV light. The particles (sintered) at 1 200 ℃ exhibited better morphology than those of a commercial product.

Control of Morphology of Ybo3 : Eu by A Mild Hydrothermal Process

Synthesis and control of the morphology of YBO3 : Eu phosphor by hydrothermal method

Particle morphology control and optical properties of hydrothermally prepared YBO3:Eu (Tb)

The concentration quenching effect in spherical YBO3:Eu 3+(Tb3+) phosphors synthesized by a mild hydrothermal process

Synthesis and photoluminescence of Eu3+-doped (Y,Gd)BO3 phosphors by a mild hydrothermal process

Synthesis of (y,gd)bo_3∶eu with Identical Spherical Morphology for PDP

Synthesis multifarious morphologies and sizes of YBO3:Eu3+ phosphors, and clarification of the crystal structure of YBO3

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Hydrothermal Synthesis and Characterization of Flowerlike YBO<SUB>3</SUB>:Eu<SUP>3+</SUP>: Hydrothermal Synthesis and Characterization of Flowerlike YBO<SUB>3</SUB>:Eu<SUP>3+</SUP>

Hydrothermal Synthesis and Characterization of Flowerlike YBO_3∶Eu~(3+)

Multiple morphologies of YF 3 : Eu 3+ microcrystals: Microwave hydrothemal synthesis, growth mechanism and luminescence properties

Influence of Synthesis Conditions on the Morphologies of ReBO3 Microstructures and White Light Emission of YBO3:Eu3+ Phosphors Prepared by an Oleic Acid-Assisted Hydrothermal Method

Hydrothermal Mild Synthesis of Microrod Crystalline Yxgd2-X(Moo4)(3): Eu3+ Phosphors Derived from Facile Co-Precipitation Precursors

Circular Plate‐Based YBO3:Eu3+ Assemblies: Synthesis and Photoluminescence Properties

Hydrothermal Synthesis and Characterization of Yvo4-Based Phosphors Doped with Eu3+ Ion

Controllable Synthesis and Tunable Luminescence of Yttrium Orthoborate Microcrystals with Multiform Morphologies and Dimensions

Morphology-tailored Synthesis and Luminescent Properties of Y 2 O 3 :Eu 3+ Phosphors

The Luminescent Properties of YBO3:Eu3+nanocrystal

Hydrothermal Synthesis And Luminescent Properties Of Flower-Like Y3bo6:Eu3+

Luminescence Properties of Y 0.95− X M X Eu 0.05 B 1− Y R Y O 3 (M = Ca, Sr, Ba, Zn, Al, 0 ≤ X ≤ 0.1; R = Si, P, 0 ≤ Y ≤ 0.1) in UV and VUV Regions

Fluorescence Intensity and Color Purity Improvement in Nanosized Ybo3 : Eu