Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Fluorescence Intensity and Color Purity Improvement in Nanosized Ybo3 : Eu

Size Dependence of Luminescent Properties for Hexagonal YBO3:Eu Nanocrystals in the Vacuum Ultraviolet Region

Synthesis and Size Dependent Luminescent Properties of Hexagonal (y,gd)bo3∶eu Nanocrystals

Correlation Between Size-Dependent Luminescent Properties and Local Structure Around Eu3+ Ions in Ybo3 : Eu Nanocrystals: an Xafs Study

Hydrothermal homogeneous urea precipitation of hexagonal YBO 3:Eu3+ nanocrystals with improved luminescent properties

Microstructure and Luminescence of Yb3+-doped Fluorosilicate Glass Ceramics

Sensitized Yb3+ Luminescence of Eu3+/Yb3+‐Codoped Fluorosilicate Glass Ceramics

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS

Hydrothermal Synthesis and Characterization of Flowerlike YBO_3∶Eu~(3+)

Solvothermal route to synthesize well-dispersed YBO3:Eu nanocrystals.

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Optical Properties of Nanocrystalline Y2O3:Eu3+

Synthesis and photoluminescence of Eu3+-doped Y2Sn2O7 nanocrystals

Local Structure and Luminescence of Nanocrystalline Y2O3:Eu

New Red Phosphor with A High Color Purity: Controlled Synthesis of 3d Architectures of Yw2o6(Oh)(3) : Eu

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

A novel efficient red-emitting K7SrY2B15O30: Eu3+ phosphor with non-concentration quenching and robust thermal stability for white LEDs

Facile Synthesis and Luminescence Properties of Uniform and Well-Dispersed Yf3:Eu3+ Architectures

Controllable Synthesis and Tunable Luminescence of Yttrium Orthoborate Microcrystals with Multiform Morphologies and Dimensions

Spectrum characteristic and local structures of nanocrysalline Y2O3 :Eu3+