YF3:RE3+ (RE = Dy, Tb, Eu) Sub-microstructures: Controllable Morphology, Tunable Multicolor, and Thermal Properties
Hongxia Guan,Ye Sheng,Yanhua Song,Chengyi Xu,Xiuqing Zhou,Keyan Zheng,Zhan Shi,Haifeng Zou
DOI: https://doi.org/10.1021/acs.jpcc.7b07879
2017-01-01
Abstract:A series of emission-tunable YF3:RE3+ (RE = Dy, Tb, Eu) phosphors were first synthesized by a glutamic acid-assisted one-step hydrothermal process. The structure and morphology were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results revealed that the samples were YF3 and Na(Y1.5Na0.5)F-6 and the size and shape of the products could be tuned just by adjusting the pH values of the initial reaction solutions or by adjusting the RE3+/NaF ratio or RE3+/NaBF4 ratio. The morphologies for the products include bundlelike microstructures, fantail-like shape, microspindles, irregular bulk, walnutlike shape, irregular ellipsoidal microrods, the asymmetric hexagonal-prismatic tubular structures and irregular microrods and irregular nanoparticles and microsphere. Furthermore, the photoluminescence properties of YF3:Dy3+,Tb3+ and YF3:Tb3+,Eu3+ were investigated in detail. Blue and yellow emissions corresponding to the F-4(9/2) -> H-6(15/2) (475 nm), F-4(9/2) -> H-6(13/2) (570 nm) transition of Dy3+; blue and green emissions corresponding to the D-5(4) -> F-7(6) (488 nm), D-5(4) -> F-7(5) (542 nm) transition of Tb3+; and red emissions corresponding to the D-5(0) -> F-7(1) (591 nm), D-5(0) -> F-7(2) (614 nm), and D-5(0) -> F-7(4) (698 nm) transition of Eu3+ can be observed in YF3 host under 365 nm near-ultraviolet radiation. The energy transfer process from Dy3+ to Tb3+ and from Tb3+ to Eu3+ was demonstrated to be resonant type via a quadrupole-quadrupole mechanism. Additionally, when codoping Tb3+ with Dy3+ or Eu3+ or tridoping Dy3+, Tb3+, and Eu3+ ions in the single component, colorful emitting can be obtained, giving abundant blue, green, yellow, orange, and especially white light emission. The temperature-dependent photoluminescence for as-prepared phosphors has been investigated in detail. Importantly, it is found that the fluorescent intensity ratio of YF3:5%Dy3+,2%Tb3+,2% Eu3+ displays a linear correlation with temperature in the wide range of 298-398 K with a high sensitivity of 0.24% K-1, indicating that it could be a good candidate for ratiometric optical thermometry. All these properties indicate that the developed phosphor may potentially be used as single-component multicolor-emitting phosphors.