Creep Fracture Behavior of Dissimilar Weld Joints Between T92 Martensitic and HR3C Austenitic Steels

Jian Cao,Yi Gong,Zhen-Guo Yang,Xiao-Ming Luo,Fu-Ming Gu,Zheng-Fei Hu
DOI: https://doi.org/10.1016/j.ijpvp.2011.01.003
IF: 2.56
2011-01-01
International Journal of Pressure Vessels and Piping
Abstract:The creep fracture of T92/HR3C dissimilar weld joints is investigated. HR3C austenitic steel is welded with T92 martensitic steel to obtain a T92/HR3C weld joint. After welding, creep tests are carried out at 625 degrees C in the stress range 110-180 MPa. The results indicate that the creep fracture mechanism is dependent on stress. When stresses >= 140 MPa, the fracture location is at the 192 base material and the connection of adjacent dimples results in transcrystalline fracture. For stresses < 140 MPa, the fracture location is at the 192 coarse-grained heat affected zone and growth of M23C6 particles as well as Laves phase (Fe-2(W, Mo)) precipitation on the grain boundaries leads to intergranular fracture. (C) 2011 Elsevier Ltd. All rights reserved.
What problem does this paper attempt to address?