Mechanisms for Creep Rupture of 12cr/alloy 4715 Dissimilar Weldments

Wuxing Ou,Jiankun Xiong,Xue Li,Fuheng Nie,Ting Li,Guijun Mao,Jianping Yang,Jian Xu,Lin Yang,Xinjian Yuan
DOI: https://doi.org/10.1016/j.engfailanal.2022.106945
IF: 4
2023-01-01
Engineering Failure Analysis
Abstract:The mechanism for creep rupture of 12%Cr /alloy 4715 welded joints was investigated by employing traditional uniaxial tensile creep in this study. The creep tests were maintained at 580 degrees C with creep loading stresses gradually decreasing from 300 to 240 MPa, and the time to failure was tested. The rupture location shifts from base metal (BM) to BM + fusion line (FL) then to FL + fine grain zone + coarse grain zone (CGZ), and finally to FL + CGZ as holding time in-creases. Meanwhile, a softening phenomenon is also observed in the heat-affected zone (HAZ) in crept specimens for a more extended holding time, where voids, carbides, and dislocation density are further discussed. The carbides are identified as Cr and Mo-rich M23C6 type, which forms mainly at grain boundaries during creep testing. In HAZ, M23C6 gradually increases and coarsens, providing nucleation sites for creep voids. Finally, the Larson-Miller parameter method is employed to provide a theoretical reference for predicting use cases that satisfy the industry service condition.
What problem does this paper attempt to address?