Research on the creep damage and interfacial failure of dissimilar metal welded joint between 10Cr9Mol VNbN and 12CrlMoV steel

Jianqiang Zhang,Haiyan Zhao,Sujuan Wu,Anli Lu,Yuhua Wang,Yinglin Zhang

2004-01-01

Abstract:The mechanical properties, creep damage, creep rupture strength and features of interfacial failures of welded joints between martensite (SA213T91) and pearlite steel (12Cr1MoV) have been investigated by means of argon tungsten pulsed arc welding, high temperature accelerated simulation, creep rupture, mechanical property tests and scanning electronic microscope (SEM). The research results indicate that the mechanical properties of overmatched and medium matched joint deteriorate obviously, and they are susceptible to creep damage and failure after accelerated simulation operation 500 h, in the condition of preheat 250°C, and post welding heat treatment 750°C × 1 h. However, the mechanical properties of undermatched joint are the best, the interfacial failure tendency of undermatched welded joint is less than those of medium and overmatched welded joint. Therefore, it is reasonable that low alloy material TR31 is used as the filler metal of weld between SA213T91 and 12Cr1MoV steel.