Abstract:This paper investigates the effect of the variation in alkoxide precursor ratio and templating agent concentration on the production of titanium silicalite (TS-1) through analysis using various physical characterisation techniques. X-ray diffraction showed clear evidence for the MFI zeolite structure and a high degree of crystallinity in all systems. For those materials prepared using a templating agent with ultra low alkali metal content, excellent agreement with previously reported unit cell parameters was obtained. For these same systems, 20% higher specific surface areas were also obtained by nitrogen adsorption. Analysis using an energy dispersive x-ray spectrometer coupled to a scanning electron microscope showed that the product typically contained between 60 and 90% of the titanium in the precursor and some dependence of titanium incorporation on the initial mixture composition was also observed. The results from Raman spectroscopy indicated titanium incorporation into the silicalite framework for all systems. For those materials produced using a templating agent with low alkali metal content, extra-framework anatase titanium dioxide was also identified at moderate Ti : Si mole ratios (>0.03) in the initial mixture. Due to its lower penetration depth, x-ray photoelectron spectroscopy (XPS) was used to characterise the titanium species in the surface layer. The XPS results indicated that a small amount of extra-framework titania was present in the surface of most of the TS-1 samples and the proportion of extra-framework material was observed to increase with both precursor alkali metal content and precursor titanium to silicon ratio.

Synthesis of a new titanosilicate: an analogue of the mineral penkvilksite

Synthesis and characterization of a novel microporous titanosilicate with a structure of penkvilksite-1M

Synthesis and characterization of titanium silicate molecular sieves with zorite-type structure

Synthesis and Characterization of a Novel Microporous Titanosilicate JLU-1

Synthesis, Structure Characterization, and Ion Exchange Properties of a Novel Open-Framework Ecomaterial Silicotitanate

Synthesis and characterization of titanium silicalite TS-1 prepared using phosphonium ions

Novel Synthesis of Ordered Mcm-41 Titanosilicates with Very High Titanium Content Via Ultrasound Radiation

Synthesis and Characterization of a Fluorotitanophosphate (nh4)0.16k1.84[ti2f2(po4)2(po3oh)] with a Unique Lamella Framework.

Characterization of titania silicalites

Synthesis of Ti-containing mesoporous silicates from inorganic titanium sources

Ordered mesoporous titanosilicates with catalytically stable and active four-coordinated titanium sites.

Synthesis of Nanoporous Titanosilicates and Their Structural Characterization by Physical Nitrogen Adsorption

Synthesis, Characterization and Catalytic Performance of Ti-Containing Mesoporous Molecular Sieves Assembled from Titanosilicate Precursors

Cooperative Structure-Directing Effects in the Synthesis of a Low-Silica Zeolite Phillipsite Analogue

Studies on the synthesis of titanium silicalite, TS-1

Titania Polymorphs Derived from Crystalline Titanium Diboride

Ti-MCM-41 synthesized from colloidal silica and titanium trichloride: Synthesis, characterization, and catalysis

Mineralogical and Optical Characterization of SiO2‐, N‐, and SiO2/N‐Co‐Doped Titania Nanopowders

The synthesis and characterization of titanium silicalite-1

Direct Synthesis and Characterization of Titanium-Substituted Mesoporous Molecular Sieve Sba-15

Titanium species in titanium silicalite TS-1 prepared by hydrothermal method