Abstract:ZnO nano-arrays were successfully prepared on silicon substrates with seed film by hydrothermal inversion growth method. The seed films prepared by magnetron sputtering are generally suitable for the preparation of perfect ZnO nano-array films. The effect of solution concentration, reaction time and hydrothermal temperature on the morphology were analyzed systematically. For the ZnO nano-arrays prepared at the same temperature, the arrays cultivated in low-concentration growth solution were arranged neatly, the morphology was regular and the cross sections were hexagonal. With the concentration increasing, the nano-rods got longer and their tops became thinner. Prolonging the hydrothermal aging time helps optimize the morphology of the nano-arrays, which is very important for subsequent device preparation. Increasing hydrothermal temperature can shorten the aging time and effectively resist the environmental difference in different directions of the nano-rods, which can promote the disappearance of the upper tips and the formation of perfect nano-rod arrays. All the phenomena are determined by the growth mechanism of the ZnO nano-array. The growth mechanism was deduced in this paper according to the growing patterns reflected in experiments. The UV light emission of ZnO nano-array at 370 nm shows a certain regularity and the regularity is related to the change of morphology with solution concentration and hydrothermal temperature. This is very important for developing the application in optoelectronic devices.

Position and density control in hydrothermal growth of ZnO nanorod arrays through pre-formed micro/nanodots.

Density-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Effect of UV irradiation on the properties of ZnO nanorod arrays prepared by hydrothermal method

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Facile and Controllable Growth of ZnO 1D Nanostructure Arrays on Zn Substrate by Hydrothermal Process

Room-temperature nonequilibrium growth of controllable ZnO nanorod arrays

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Anodic-Aluminium-Oxide Template-Assisted Growth Of Zno Nanodots On Si (100) At Low Temperature

Ordered Growth and Photoluminescence of ZnO Nano-Arrays on Silicon Substrates with Seed Film by Hydrothermal Method

Low-temperature hydrothermally grown 100 μm vertically well-aligned ultralong and ultradense ZnO nanorod arrays with improved PL property

Low temperature growth and properties of ZnO nanorod arrays

Controllable growth and optical properties of ZnO nanostructures on Si nanowire arrays

Growth mechanism and diameter control of well-aligned small-diameter ZnO nanowire arrays synthesized by a catalyst-free thermal evaporation method.

Density-controlled Electrodeposition Growth of Zinc Oxide Nanorod Arrays.

Growth of flower-like ZnO on ZnO nanorod arrays created on zinc substrate through low-temperature hydrothermal synthesis

Controlled Growth of Well-Aligned Zno Mirco/Nanorod Arrays on Gan Substrates Using A Novel Solution Method

Controllable Growth of Highly Ordered ZnO Nanorod Arrays Via Inverted Self-Assembled Monolayer Template.

ZnO Nanorod Arrays: Field-assisted Growth in Aqueous Solution and Field Emission Properties

Mechanical-Agitation-Assisted Growth of Large-Scale and Uniform ZnO Nanorod Arrays Within 3D Multichannel Monolithic Substrates