Abstract:Micro relative sliding exists on the contact surface of the main primary equipment's surface structures, resulting in serious fretting fatigue. The plastic effect causes serious fatigue to the structure under alternating loads. Existing fatigue life prediction models fail to fully consider the shortcomings of fretting and plastic effects, which causes the prediction results to be significantly different to real-lifeworld in engineering situations. Therefore, it is urgent to establish a fretting damage fatigue life prediction model of contact structures which considers plastic effects. In this study, a plastic fretting fatigue life prediction model was established according to the standard structural contact theory. The location of dangerous points was evaluated according to a finite element simulation. The cyclic load maximum stress value was compared with the fretting fatigue test data to confirm the error value, and the error between the proposed fretting fatigue life model and the test value was within 15%. Concurrently, we combined this with mass data analysis and research, as it is known that the contact zone parameters have an impact on fretting fatigue and affect the structural lifespan. With the help of ABAQUS, the fretting numerical calculation of the dovetail tenon model was carried out to analyze the sensitive factors affecting the fretting fatigue life of the dovetail tenon structure. By keeping the fretting load unchanged, the contact area parameters such as contact surface form, contact area width and friction coefficient were changed in order to calculate the fretting stress value, σfretting and the dovetail structure was improved to extend its fretting fatigue life. Finally, it was concluded that fretting fatigue was most sensitive to the width and contact form of the contact area. In actual engineering design, multiple factors should be considered comprehensively to determine a more accurate and suitable width and form of the contact area. For the selection of friction coefficient, on the premise of saving costs and meeting the structural strength requirements, the friction coefficient should be as small as possible, and the problem can also be solved through lubrication during processing.

Predicting the Fretting Fatigue Strength and Life of Titanium Alloys

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Prediction of Fatigue Life for Automotive A-Alloy Wheel with Integrated Cast Defects

Fretting Fatigue Damage of Titanium Alloy Clinched Structure

A Debris Layer Evolution-Based Model for Predicting Both Fretting Wear and Fretting Fatigue Lifetime

Microstructural evolution and oxidation in α/β titanium alloy under fretting fatigue loading

Fretting Fatigue Life Prediction of Dovetail Structure Based on Plastic Effect and Sensitivity Analysis of Influencing Factors

Fretting fatigue crack initiation and propagation behaviours of Ti6Al4V alloy coated by functionally graded material

Fretting Fatigue Life Model Under Combined Loading

Experimental and computational investigation of fretting fatigue characterized by nominal contact pressure in dovetail structures

Subsurface deformation mechanism and the interplay relationship between strength-ductility and fretting wear resistance during fretting of a high-strength titanium alloy

The Effect of Defect Characteristics on Prediction of Fatigue Life of TC4 Titanium Alloy Welded Joints

Preparation and Study on Fretting Tribological Behavior of Composite Lubrication Structure on the Titanium Alloy Surface

Ti-6Al-4V fretting wear and a quantitative indicator for fretting regime evaluation

Life prediction method based on damage mechanism for titanium alloy TC4 under multiaxial thermo-mechanical fatigue loading

Predicting dwell fatigue life in titanium alloys using modelling and experiment

Dependence of fretting wear on the microstructure characteristics and impact on the subsurface stability of a metastable β titanium alloy

Experimental study of fretting fatigue in dovetail assembly considering temperature effect based on damage mechanics method

Continuum damage mechanics-based fatigue life prediction of L-PBF Ti-6Al-4V

Experimental and Numerical Investigations of Fretting Fatigue Behavior for Steel Q235 Single-Lap Bolted Joints

Variable cycle fretting conditions meditated wear behavior and mechanism in a self-lubricating composite coating on TC21 titanium alloy substrate